: Obtención de precursores para catalizadores empleando pilas alcalinas desechadas como materia prima haciendo uso de ácido acético

Lopez Vega, Maria Jose; Giraldo Ardila, Bayrón Alexis

: Obtención de precursores para catalizadores empleando pilas alcalinas desechadas como materia prima haciendo uso de ácido acético

dc.contributor.advisor	Delvasto Angarita, Pedro Luis
dc.contributor.author	Lopez Vega, Maria Jose
dc.contributor.author	Giraldo Ardila, Bayrón Alexis
dc.contributor.evaluator	Ardila Santamaria, Nadia Angarita
dc.contributor.evaluator	Pinto Silva, Laura Fernanda
dc.date.accessioned	2023-05-29T19:24:27Z
dc.date.available	2023-05-29T19:24:27Z
dc.date.created	2023-05-27
dc.date.embargoEnd	2028-05-27
dc.date.issued	2023-05-27
dc.description.abstract	En el presente proyecto de grado, se recuperaron óxidos de zinc y manganeso de pilas alcalinas desechadas, empleando una combinación de procesos hidrometalúrgicos, cristalización evaporativa y calcinación, con el objeto de, a futuro, emplearlos en la producción de catalizadores. Se realizaron pruebas de lixiviación tanto para la pasta anódica como para la pasta catódica de pilas alcalinas desechadas, utilizando soluciones de ácido acético, y se ajustaron parámetros experimentales como la temperatura, concentración del ácido y presencia de aditivos. La variable de respuesta para las lixiviaciones de manganeso fue el color de la disolución, evaluado mediante UV-VIS, y se encontró una mayor absorbancia en las pruebas realizadas a temperatura de 27º C con una concentración de ácido de 4 M, y empleando como aditivos acido nítrico y polvo de hierro cero-valente. Por otro lado, para el zinc, la variable de respuesta fue el tiempo de disolución, donde se obtuvo un tiempo (15 min) de disolución menor en las pruebas realizadas a 70ºC con una concentración de 4 M. La eficiencia para la extracción de Mn fue de 50,78% y para el zinc 100%. Las soluciones obtenidas durante la lixiviación se sometieron a cristalización, obteniéndose exitosamente acetatos de zinc y manganeso que, posteriormente, se sometieron a un proceso de calcinación en una mufla a una temperatura de 600 y 900 º C durante 6 horas para la obtención de sus óxidos. Los óxidos obtenidos se caracterizaron mediante FTIR, en el cual indicaron que la mejor temperatura para obtenerlos fue de 900 °C.
dc.description.abstractenglish	In this undergraduate project, zinc and manganese oxides were recovered from discarded alkaline batteries using a combination of hydrometallurgical processes, evaporative crystallization, and calcination, with the aim of using them in the production of catalysts in the future. Leaching tests were carried out for both the anodic and cathodic paste of discarded alkaline batteries using acetic acid solutions, and experimental parameters such as temperature, acid concentration, and the presence of additives were adjusted. The response variable for manganese leaching was the color of the solution, evaluated using UV-VIS, and higher absorbance was found in tests carried out at a temperature of 27°C with an acid concentration of 4M, using nitric acid and zero-valent iron powder as additives. On the other hand, for zinc, the response variable was the dissolution time, where a lower dissolution time (15 min) was obtained in tests carried out at 70°C with a concentration of 4M. The efficiency for Mn extraction was 50.78% and for zinc 100%. The solutions obtained during leaching were subjected to crystallization, successfully obtaining zinc and manganese acetates which were then subjected to a calcination process in a muffle furnace at a temperature of 600 and 900°C for 6 hours to obtain their respective oxides. The obtained oxides were characterized using FTIR, which indicated that the best temperature to obtain them was 900°C
dc.description.degreelevel	Pregrado
dc.description.degreename	Ingeniero Metalúrgico
dc.format.mimetype	application/pdf
dc.identifier.instname	Facultad de Ingeníerias Fisicoquímicas
dc.identifier.reponame	Escuela de Ingeniería Metalúrgica y Ciencia de Materiales
dc.identifier.repourl	https://noesis.uis.edu.co
dc.identifier.uri	https://noesis.uis.edu.co/handle/20.500.14071/14434
dc.language.iso	spa
dc.publisher	Universidad Industrial de Santander
dc.publisher.faculty	Ingeniería Metalúrgica
dc.publisher.program	Universidad Industrial de Santander
dc.publisher.school	Universidad Industrial de Santander
dc.rights	info:eu-repo/semantics/openAccess
dc.rights.accessrights	info:eu-repo/semantics/openAccess
dc.rights.coar	http://purl.org/coar/access_right/c_abf2
dc.rights.creativecommons	Atribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.license	Attribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.uri	http://creativecommons.org/licenses/by-nc-nd/4.0/
dc.subject	Precursores para catalizadores
dc.subject	lixiviación
dc.subject	reciclaje pilas alcalinas
dc.subject	cristalización
dc.subject	Calcinacion
dc.subject.keyword	Leaching
dc.subject.keyword	Precursors for catalysts
dc.subject.keyword	alkaline battery recycling
dc.subject.keyword	crystallization
dc.subject.keyword	calcination
dc.title	: Obtención de precursores para catalizadores empleando pilas alcalinas desechadas como materia prima haciendo uso de ácido acético
dc.title.english	Obtaining precursors for catalysts using discarded alkaline batteries as raw material using acetic acid
dc.type.coar	http://purl.org/coar/resource_type/c_7a1f
dc.type.hasversion	http://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.local	Tesis/Trabajo de grado - Monografía - Pregrado
dspace.entity.type