Determinación de la velocidad de corrosión de un acero API 5L- X42 en agua de mar sintética.

Flórez Oviedo, Yenny Fernanda; Roncallo Cervantes, Liz María

Determinación de la velocidad de corrosión de un acero API 5L- X42 en agua de mar sintética.

dc.contributor.advisor	Peña Ballesteros, Dario Yesid
dc.contributor.author	Flórez Oviedo, Yenny Fernanda
dc.contributor.author	Roncallo Cervantes, Liz María
dc.contributor.evaluator	Laverde Cataño, Dionicio Antonio
dc.contributor.evaluator	Gómez Ramírez, Javier Enrique
dc.date.accessioned	2024-02-27T22:38:31Z
dc.date.available	2024-02-27T22:38:31Z
dc.date.created	2024-02-26
dc.date.issued	2024-02-26
dc.description.abstract	Pretende obtener más información sobre cómo afecta la velocidad de corrosión al acero API 5L- X42 cuando está en contacto con un medio de agua de mar (sintética). El objetivo principal es analizar la calidad del acero API 5L -X42 cuando se utiliza en tuberías de la industria petroquímica, en su comportamiento electroquímico, para comprender cómo responde este material a la corrosión en agua de mar sintética simulada, con iones de cloruro conocidos por ser agresivos. El análisis mediante diferentes tiempos de inmersión para evaluar la respuesta del acero a largo plazo en contacto directo con este entorno sintético y una prueba en un entorno real de agua de mar en tiempo cero, para estudiar las respuestas de los tiempos cero tanto en el medio sintético como el medio real (traída de Cartagena). Un proceso de desbaste en los cupones de acero para lograr una superficie homogénea, mejorando los resultados al exponer el acero a una solución marina simulada durante un periodo de treinta días. Cinco cupones fueron sometidos a intervalos de tiempos diferentes. Aplicando técnicas electroquímicas, incluyendo Resistencia a la Polarización (Rp), Tafel, potencial de corrosión, se observó la microestructura a través de SEM y DRX para estudiar la corrosión generalizada. Los resultados mostraron la variación de la velocidad de corrosión a partir de las curvas Tafel y respuestade la RP a partir de las pendientes de esa curva se obtuvo para ambas técnicas que la tendencia de la velocidad de corrosión para los cupones era disminuir a medida que pasaba el tiempo ya que la densidad de corriente mostro una tendencia decreciente, atribuible a la formación de productos de corrosión que actuaron como obstáculos para la difusión de iones de cloruro, hidróxido y sulfuro hacia la superficie del acero. Por medio de las técnicas de SEM y DRX se evidenció que el elemento Cl presente en el agua de mar sintética era el responsable mayoritariamente de la formación de la corrosión; además, las morfologías observadas proporcionaron detalles sobre la capa de óxido formada y los productos de corrosión formados en el cupón de 30 días de exposición.
dc.description.abstractenglish	The present research aims to obtain more information on how the corrosion rate of API 5L -X42 steel is affected when it is in contact with a seawater (synthetic) medium. The main objective of this study is to analyze the quality of API 5L X42 steel when used in petrochemical industry pipelines, focusing on its electrochemical behavior, it seeks to understand how this material responds to corrosion in simulated synthetic seawater, with chloride ions known to be aggressive. The analysis is performed at different immersion times to evaluate the long-term response of the steel in direct contact with this synthetic environment. First, a roughing process was carried out on the steel coupons to achieve a homogeneous surface, thus improving the results by exposing the steel to a simulated marine solution for a period of thirty days. Five coupons were subjected to different time intervals. Subsequently, electrochemical techniques were applied, including Polarization Resistance (Rp), Tafel, corrosion potential, and the microstructure was observed through SEM and XRD to study generalized corrosion. The results showed the variation of the corrosion rate using Tafel curves and the polarization resistance (RP) response. For both techniques, it was observed that the trend of corrosion rate the coupons decreased over time. This was attributed to the decreasing current density, which was caused by the formation of corrosion products acting as barriers to the diffusion of chloride, hydroxide, and sulfide ions towards the steel surface. SEM and XRD techniques showed that the Cl element present in the synthetic seawater was responsible for the corrosion formation; in addition, the morphologies observed provided details about the oxide layer formed and the corrosion products formed in the 30-day coupon.
dc.description.degreelevel	Pregrado
dc.description.degreename	Ingeniero Químico
dc.format.mimetype	application/pdf
dc.identifier.instname	Facultad de Ingeníerias Fisicoquímicas
dc.identifier.reponame	Escuela de Ingeniería Química
dc.identifier.repourl	https://noesis.uis.edu.co
dc.identifier.uri	https://noesis.uis.edu.co/handle/20.500.14071/15892
dc.language.iso	spa
dc.publisher	Universidad Industrial de Santander
dc.publisher.faculty	Facultad de Ingeníerias Fisicoquímicas
dc.publisher.program	Ingeniería Química
dc.publisher.school	Escuela de Ingeniería Química
dc.rights	info:eu-repo/semantics/openAccess
dc.rights.accessrights	info:eu-repo/semantics/openAccess
dc.rights.coar	http://purl.org/coar/access_right/c_abf2
dc.rights.creativecommons	Atribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.license	Atribución-NoComercial-SinDerivadas 2.5 Colombia (CC BY-NC-ND 2.5 CO)
dc.rights.uri	http://creativecommons.org/licenses/by-nc-nd/4.0/
dc.title	Determinación de la velocidad de corrosión de un acero API 5L- X42 en agua de mar sintética.
dc.title.english	Determination of the corrosion rate of an API 5L-X42 steel in synthetic seawater.
dc.type.coar	http://purl.org/coar/resource_type/c_7a1f
dc.type.hasversion	http://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.local	Tesis/Trabajo de grado - Monografía - Pregrado