Influencia del modo de transferencia por arco pulsado en el proceso GMAW sobre las propiedades mecánicas y microestructurales de un acero ASTM A-36

Simple item page
dc.contributor.advisorÁlvarez Orozco, Hernán
dc.contributor.advisorRincón Ortiz, Mauricio
dc.contributor.advisorCardona Granados, Afranio Antonio
dc.contributor.authorOlivero Monsalve, Eduardo Santos
dc.date.accessioned2024-03-03T23:21:59Z
dc.date.available2017
dc.date.available2024-03-03T23:21:59Z
dc.date.created2017
dc.date.issued2017
dc.description.abstractEl presente trabajo estudia la influencia de la pulsación de la corriente en la transferencia de cortocircuito para la soldadura GMAW sobre el acero estructural ASTM A36. Se obtuvieron uniones soldadas planas con bisel tipo V usando la transferencia de cortocircuito convencional y cortocircuito con arco pulsado con una mezcla de gas 75 % Argón 25 as cuales fueron comparadas entre sí, analizando los cambios microestructurales y de propiedades mecánicas. La microestructura del material A36 es una matriz ferrítica con granos de perlita, típica de un acero hipoeutectoide, mientras que la microestructura de la soldadura con cortocircuito fue una matriz de perlita suave con ferrita en los límites de grano y la microestructura de la soldadura de cortocircuito con arco pulsado presentó ferrita acicular en los límites de grano, esto debido a que la transferencia pulsada aportó un calor menor generando velocidades de enfriamiento rápidas. La transferencia de calor para la soldadura de cortocircuito convencional fue calculada y se obtuvo un valor de 0.47 [kJ/pul] que es un aporte de calor bajo, característico de la transferencia cortocircuito; el calor aportado por la transferencia con arco pulsado es menor a este valor debido a que en los ciclos del pulso donde la corriente máxima decrece a alcanzar la corriente mínima se genera un enfriamiento que disminuye la transferencia de calor, generando que el depósito de metal presente un gradiente de temperatura alto y el metal se enfrié rápidamente. Los resultados en las pruebas mecánicas de tracción, doblez, impacto se conectaron con las microestructuras observadas en donde los resultados satisfactorios los consiguió la soldadura convencional.
dc.description.abstractenglishThe present work studies the influence of current pulsation on short-circuit transfer for GMAW welding on structural steel ASTM A-36. V-type bevelled flat welds were obtained using conventional short-circuit transfer and pulsed arc short-circuit with a 75% Argon-25% mechanical properties. The microstructure of the base material is a ferrite matrix with perlite grains, typical of a medium carbon hypoeutectoid steel, where the microstructure of the short-circuit transfered welding was a pearlite matrix with ferrite at the grain boundaries and the welding microstructure of the short-circuit with pulsed arc presented acicular ferrite at the grain boundaries. The behavior can be explained by the pulsed transfer bringing a lower generated heat which causes fast cooling rates. The heat transfer for the conventional short-circuit welding was calculated and it was of 0.47 [kJ / pul], which is a low input heat, characteristic of the short-circuit transfer. The heat provided by the pulsed arc transfer is smaller than in the conventional short-circuit welding, as a consequence of the pulsed cycles where the current after reaching its maximum value, it reduced until a minimum current. Then, a fast cooling rate is produced. The tension, bending and impact tests corroborated the above mentioned behavior, where the the values approved by ASME Codewere those obtained by the conventional transfer mode of welding.
dc.description.degreelevelPregrado
dc.description.degreenameIngeniero Metalúrgico
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/36583
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicoquímicas
dc.publisher.programIngeniería Metalúrgica
dc.publisher.schoolEscuela de Ingeniería Metalúrgica y Ciencia de Materiales
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.subjectCorriente Pulsada
dc.subjectAcero Hipoeutectoide
dc.subjectTransferencia Cortocircuito.
dc.subject.keywordPulsed Current
dc.subject.keywordHypoeutectoid Steel
dc.subject.keywordShort Circuit Transfer.
dc.titleInfluencia del modo de transferencia por arco pulsado en el proceso GMAW sobre las propiedades mecánicas y microestructurales de un acero ASTM A-36
dc.title.englishInfluence of pulsed arc transfer mode on mechanical and microstructural properties of astm a36 steel.
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_7a1f
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
381.87 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
4.46 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
318.54 KB
Format:
Adobe Portable Document Format
Download
Collections
Ingeniería Metalúrgica