Desarrollo de recubrimientos de estructura bimodal elaborados mediante proyeccion termica por combustion oxiacetilenica para aplicaciones en ambientes corrosivos y en condiciones de desgaste abrasivo

Simple item page
dc.contributor.advisorRincón Ortiz, Mauricio
dc.contributor.advisorVargas Galvis, Fabio
dc.contributor.authorVargas Galvis, Freddy
dc.date.accessioned2023-04-06T20:19:51Z
dc.date.available2023
dc.date.available2023-04-06T20:19:51Z
dc.date.created2019
dc.date.issued2019
dc.description.abstractCon el fin de proponer una alternativa para los recubrimientos de cromo duro, se depositaron polvos de SiO2-Fe2O3-Al2O3-MgO-Cr2O3 y de Al2O3-TiO2 sobre sustratos de acero al carbón AISI 1020 utilizando proyección térmica oxiacetilénica. Con el fin de fabricar las materias primas con las cuales se depositaron los recubrimientos, se atomizaron escorias de fundición y polvos de alúmina, obteniendo partículas de morfología esférica y con poros en la superficie, los cuales fueron rellenados con alúmina de tamaño nanométrico, así como partículas esféricas de alúmina, que fueron mezcladas con nanopartículas de TiO2 previamente aglomeradas. Las materias primas procesadas en el laboratorio, así como los polvos comerciales fueron caracterizadas mediante fluorescencia de rayos X (FRX), difracción de rayos X (DRX) y microscopia electrónica de barrido (MEB). Para fabricar los recubrimientos se utilizó la cámara ARESTE de la Universidad de Antioquia. Los parámetros de proyección térmica fueron ajustados para obtener recubrimientos con estructura bimodal conformada por partículas parcialmente fundidas de orden nanométrico y submicrométrico, así como partículas completamente fundidas de orden micrométrico. Se determinó el porcentaje de porosidad y se estableció si la estructura de los recubrimientos tenía características bimodales. Por su parte, la microdureza, el desempeño tribológico y la capacidad protectora de los recubrimientos se determinó mediante indentación Vickers, el método de bola sobre disco y por Espectroscopía de Impedancias Electroquímica (EIS). Con los resultados obtenidos se pudo establecer que los recubrimientos elaborados a partir de escorias de fundición y los recubrimientos de composición química AT-40, su desempeño tribológico y su capacidad para proteger al sustrato de efectos corrosivos es menor que el de los recubrimientos AT-13 de estructura bimodal, que mostraron un desempeño tribológico del mismo orden de magnitud que el del cromoduro y cuando son dispuestos como recubrimiento superior de una bicapa, su capacidad protectora a la corrosión es superior. *
dc.description.abstractenglishIn order to propose an alternative for hard chromium coatings, SiO2-Fe2O3-Al2O3-MgO-Cr2O3 and Al2O3- TiO2 powders were oxy-fuel thermally sprayed onto AISI 1020 substrates. In order to manufacture the raw materials with which the coatings were deposited, smelting slags and Al2O3 powders were atomized, obtaining spherical morphology particles and with pores on the surface, which were filled with Al2O3 of nanometric size, as well as spherical Al2O3 particles, which were mixed with previously agglomerated TiO2 nanoparticles. Raw materials processed in the laboratory, additionally as commercial powders, were characterized by X-ray fluorescence (FRX), X-ray diffraction (DRX) and scanning electron microscopy (MEB). The ARESTE chamber of the University of Antioquia was used to manufacture the coatings. The thermal projection parameters were adjusted to obtain coatings with bimodal structure formed by partially melted particles of nanometric and submicrometer order, also as completely melted particles of micrometric order. The percentage of porosity was determined, and it was established whether the structure of the coatings had bimodal characteristics. On the other hand, the microhardness, the tribological performance and the protective capacity of the coatings were determined by Vickers indentation, the ball on disk method and by Electrochemical Impedance Spectroscopy (EIS). With the results obtained, it was possible to establish that coatings made from smelting slag and coatings of chemical composition AT-40, their tribological performance and their ability to protect the substrate from corrosive effects is less than that of AT-13 coatings of bimodal structure, which showed a tribological performance with the same order of magnitude of the chrome plated and when they are arranged as an upper coating of a bilayer, its corrosion protection capacity is higher. *
dc.description.degreelevelMaestría
dc.description.degreenameMagíster en Ingeniería de Materiales
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/13990
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicoquímicas
dc.publisher.programMaestría en Ingeniería de Materiales
dc.publisher.schoolEscuela de Ingeniería Metalúrgica y Ciencia de Materiales
dc.rightsinfo:eu-repo/semantics/openAccess
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.coarhttp://purl.org/coar/access_right/c_abf2
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/4.0/
dc.subjectRecubrimientos
dc.subjectProyección Térmica
dc.subjectResistencia Al Desgaste
dc.subjectCapacidad Protectora Frente A La Corrosión
dc.subject.keywordDevelopment Of Bimodal Structure Coatings Manufactured By Oxy-Fuel Thermal Spraying For Applications In Corrosive Environments And Abrasive Wear Conditions
dc.titleDesarrollo de recubrimientos de estructura bimodal elaborados mediante proyeccion termica por combustion oxiacetilenica para aplicaciones en ambientes corrosivos y en condiciones de desgaste abrasivo
dc.title.englishDevelopment of bimodal structure coatings prepared through thermal projection by oxyacetilenic combustion for applications in corrosive environments and abrasive wear conditions*
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_bdcc
dc.type.localTesis/Trabajo de grado - Monografía - Maestría
dspace.entity.type
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
204.9 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
3.51 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
110.39 KB
Format:
Adobe Portable Document Format
Download
Collections
Maestría en Ingeniería de Materiales