Estudio del comportamiento electroquímico de la aleación ti6al4v recubierta con películas de policraprolactona/quitosano/biovidrio

Simple item page
dc.contributor.advisorPeña Ballesteros, Darío Yesid
dc.contributor.advisorSierra Uribe, Jhon Harrison
dc.contributor.authorCastro Baron, Zayda Vanessa
dc.contributor.authorVillamizar, David Ricardo
dc.date.accessioned2024-03-03T22:13:32Z
dc.date.available2015
dc.date.available2024-03-03T22:13:32Z
dc.date.created2015
dc.date.issued2015
dc.description.abstractSe estudió el comportamiento electroquímico de la aleación Ti6Al4V recubierta con películas de policaprolactona/quitosano/biovídrio en un fluido corporal simulado (SBF) a 36.5°C, y comparado con recubrimientos individuales de policaprolactona/quitosano y biovídrio. Para ello, se prepararon soluciones estables de policaprolactona/quitosano y por medio de la técnica dipcoating se obtuvieron recubrimientos sobre sustratos de Ti6Al4V, que presentaban una superficie rugosa obtenida con papel abrasivo # 240, seguido y por medio del proceso sol-gel se obtuvieron soles estables de biovídrio 45S5, el cual fue sinterizado a 700°C y molido para obtener polvo de 52 micras, posteriormente se formó una suspensión de polvo de biovídrio en un sol estable de 45S5 y se recubrieron sustratos de Ti6Al4V que ya tenían películas de policaprolactona/quitosano, finalmente fueron llevadas a un tratamiento térmico a 100°C por medio hora. La morfología y formación de fosfatos de calcio fue caracterizada por microscopia electrónica de barrido (SEM) y espectroscopia de energía dispersa (EDS), mientras que la caracterización electroquímica se realizó mediante las técnicas de resistencia a la polarización lineal, polarización potenciodinámica y espectroscopia de impedancia electroquímica (EIS). De los análisis SEM-EDS se determinó que la película base de policaprolactona/quitosano disminuyó el agrietamiento de la capa de biovídrio, en el recubrimiento mixto, el cual presentó precipitados blancos con relaciones Ca/P entre 1.4-1.5 que corresponden a apatitas amorfas. Los resultados de las pruebas electroquímicas evidenciaron que el recubrimiento mixto presentó valores de impedancia, resistencia a la polarización y velocidad de corrosión menores que los mostrados por el recubrimiento de policaprolactona/quitosano, quien fue el que mostró mayor protección, mientras que el biovídrio fue el que menos protegió a la aleación Ti6Al4V.
dc.description.abstractenglishThe electrochemical behavior of Ti6Al4V alloy coated with film polycaprolactone/chitosan/bioglass in a simulated body fluid (SBF) at 36.5 ° C was studied, and compared with individual coatings polycaprolactone/chitosan and bioglass. For this, stable solutions of polycaprolactone/chitosan were prepared and through dipcoating technique coatings on Ti6Al4V substrates, which had a rough surface obtained with abrasive paper # 240 were obtained, followed and by the sol-gel process stable sols were obtained bioglass 45S5, which was sintered at 700 ° C and ground to obtain powder of 52 microns, then a suspension of powder bioglass formed in a stable sol of 45S5 and substrates Ti6Al4V already had coated films polycaprolactone/chitosan were, finally taken to a heat treatment at 100 ° C for half an hour. The morphology and formation of calcium phosphates was characterized by scanning electron microscopy (SEM) and spectroscopy energy dispersive (EDS), while the electrochemical characterization was performed using techniques resistance to linear polarization, potentiodynamic polarization and impedance spectroscopy electrochemical (EIS). From the SEM-EDS analysis it was determined that the base film polycaprolactone/chitosan decreased cracking layer bioglass, in the mixed coating, which provided white precipitates with Ca/P relationship between 1.4-1.5 corresponding to amorphous apatites. The electrochemical tests results showed that the mixed coating showed values of impedance and polarization resistance corrosion rate lower than that shown by the coating of polycaprolactone / chitosan, who was showed better protection while bioglass was less protected the alloy Ti6Al4V.
dc.description.degreelevelPregrado
dc.description.degreenameIngeniero Metalúrgico
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/33292
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicoquímicas
dc.publisher.programIngeniería Metalúrgica
dc.publisher.schoolEscuela de Ingeniería Metalúrgica y Ciencia de Materiales
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.subjectTi6Al4V
dc.subjectPolicaprolactona
dc.subjectQuitosano
dc.subjectBiovídrio
dc.subjectComportamiento Electroquímico.
dc.subject.keywordTi6Al4V
dc.subject.keywordPolycaprolactone
dc.subject.keywordChitosan
dc.subject.keywordBioglass
dc.subject.keywordElectrochemical Behavior.
dc.titleEstudio del comportamiento electroquímico de la aleación ti6al4v recubierta con películas de policraprolactona/quitosano/biovidrio
dc.title.englishStudy electrochemical behavior of ti6al4v alloy films coated with polycaprolactone/chitosan/bioglass.
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_7a1f
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
270.54 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
3.58 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
205.84 KB
Format:
Adobe Portable Document Format
Download
Collections
Ingeniería Metalúrgica