Caracterizacion electroquimica de electrodos de nanofibras de carbono sustentadas en matriz de niquel fabricados por molienda mecanica para su utilizacion en almacenamiento de hidrogeno

Simple item page
dc.contributor.advisorUribe Perez, Ivan
dc.contributor.authorBecerra Pinto, Sandra Milena
dc.contributor.authorDuarte Herrera, Johanna Patricia
dc.contributor.authorHormiga Castellanos, Cesar Augusto
dc.date.accessioned2024-03-03T04:39:41Z
dc.date.available2004
dc.date.available2024-03-03T04:39:41Z
dc.date.created2004
dc.date.issued2004
dc.description.abstractSe caracterizaron electrodos de nanofibras de carbono sustentadas en matriz de níquel utilizando técnicas electroquímicas de voltametría cíclica y pulsos galvanostáticos con el fin de determinar los parámetros cinéticos del material utilizado y además caracterización por difracción de rayos X para determinar cualitativamente las fases presentes en las muestras. Se fabricaron electrodos con 1, 2 y 3% de nanofibras de carbono con y sin tratamiento químico sustentadas en matriz de níquel por la técnica de molienda mecánica en un molino attritor con variaciones de tiempos de molienda de 6,12 y 24 horas, corrientes carga/descarga galvanostática entre 1 y 100 mA y tiempos de carga entre 0.5 y 24 horas. Para estos electrodos se determinaron los parámetros cinéticos: capacidad de almacenamiento, reversibilidad, velocidad de descarga y vida al ciclado utilizando las técnicas electroquímicas de voltametría cíclica y pulsos galvanostáticos carga Œdescarga. Las mejores condiciones en cuanto a los parámetros cinéticos se obtuvieron para los electrodos con 1% de nanofibras de carbono atacadas químicamente con ácido nítrico 5M, con 6 horas de molienda, sometidos a una corriente carga/descarga de 10 mA. Estos electrodos se caracterizaron por difracción de rayos X, técnica con la cual se detectó níquel parcialmente amorfo y carbono totalmente amorfo. La máxima capacidad de almacenamiento encontrada fue 1180.11 mAh/g equivalente a 4.18 wt% de hidrógeno para un tiempo de carga de 1.5 horas, reversibilidad de 0.79 y con una durabilidad al ciclado de 26 ciclos.
dc.description.abstractenglishCarbon nanofibers electrodes sustained in nickel's die were characterized using electrochemical techniques of cyclic voltammetry and galvanostatic pulses with the purpose of determining the kinetic parameters of the used material and also characterization by XŒray diffraction to determinate the present phases qualitatively in the samples. Electrodes were manufactured with 1, 2 y 3% of carbon nanofibers with and without chemical treatment sustained in nickel's die by ball milling technique in a attritor mill with variations of times of milling by 6, 12 and 24 hours, galvanostatic charge/discharge current between 1 and 100 mA and charge times between 0.5 and 24 hours. For these electrodes were determined storage capacity, reversibility, discharge rate and life to the cycled using the electrochemical techniques of cyclic voltammetry and charge/discharge galvanostatic pulse. The best conditions for the kinetic parameters were obtained for the electrodes with 1% of carbon nanofibers attacked chemically with nitric acid 5M, with 6 hours of ball milling subjected to a charge/discharge current of 10 mA. These electrodes were characterized by XŒray diffraction, technique with which was detected partially amorphous nickel and completely amorphous carbon. The maximum storage capacity was 1180.11 mAh/g equivalent to 4.18 wt% of hydrogen for charge time of 1.5 hours, reversibility of 0.79 and with durability to the cycled of 26 cycles.
dc.description.degreelevelPregrado
dc.description.degreenameIngeniero Metalúrgico
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/16535
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicoquímicas
dc.publisher.programIngeniería Metalúrgica
dc.publisher.schoolEscuela de Ingeniería Metalúrgica y Ciencia de Materiales
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.subjectNanofibras de carbono
dc.subjectMolienda mecánica
dc.subjectAlmacenamiento de hidrógeno.
dc.subject.keywordCarbon nanofibers
dc.subject.keywordBall milling
dc.subject.keywordHydrogen storage.
dc.titleCaracterizacion electroquimica de electrodos de nanofibras de carbono sustentadas en matriz de niquel fabricados por molienda mecanica para su utilizacion en almacenamiento de hidrogeno
dc.title.englishElectrochemical characterization of carbon nanofibers electrodes sustained in nickel's die manufactured by ball milling for their use in hydrogen storage.
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_7a1f
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
Files
Original bundle
Now showing 1 - 2 of 2
No Thumbnail Available
Name:
Documento.pdf
Size:
2.48 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
577.22 KB
Format:
Adobe Portable Document Format
Download
Collections
Ingeniería Metalúrgica