Síntesis y caracterización de electrodos de b-tio2/ti para la oxidación fotoelectrocatalítica de glicerol bajo luz visible

Simple item page
dc.contributor.advisorNiño Gómez, Martha Eugenia
dc.contributor.advisorPedraza Avella, Julio Andrés
dc.contributor.advisorGualdron Reyes, Andrés Fabian
dc.contributor.authorMancilla Rueda, Federico Josue
dc.contributor.authorRojas Vargas, Silvia Fernanda
dc.date.accessioned2024-03-03T22:10:21Z
dc.date.available2015
dc.date.available2024-03-03T22:10:21Z
dc.date.created2015
dc.date.issued2015
dc.description.abstractLa fotoelectrocatálisis es una técnica ampliamente utilizada en procesos de saneamiento ambiental y producción de energía debido a la alta capacidad oxidativa/reductiva que presenta. En este trabajo se establecieron los valores más apropiados para determinadas variables durante la elaboración de películas de TiO2 dopadas con boro sobre titanio, preparadas por el método sol-gel y depositadas sobre el sustrato por inmersión, empleadas como electrodo de trabajo. Se evaluó el efecto de la cantidad de agua (0,3, 0,7 y 1,1mL), las capas de la película (1, 2 y 3 capas) y la rampa de calentamiento (1, 3 y 5 °C/min) sobre la actividad del material. Las películas fueron caracterizadas por Microscopia Electrónica de Barrido de Emisión de Campo, Espectroscopia Raman y Espectroscopía de Reflectancia Difusa UV-Vis. Las propiedades fotoelectrocatalíticas fueron estudiadas mediante mediciones de voltamperometría bajo luz visible. Los resultados muestran que los parámetros finales que más afectan la actividad de las películas son el espesor y la uniformidad, que se ven modificados por todas las variables estudiadas y que condicionan el transporte de electrones. Las condiciones para las que se obtuvieron mejores propiedades fueron 0,7 mL de agua, 1 capa de película y 3°C/min como velocidad de calentamiento. Adicionalmente, se comprobó que el dopaje con B modifica en ancho de banda de las películas aumentando la actividad bajo luz visible. Se evaluó la actividad fotoelectrocatalítica del material en la degradación de un compuesto orgánico (glicerol) obteniendo una degradación de 25% en un tiempo de 2 horas.
dc.description.abstractenglishPhotoelectrocatalysis is a technique widely used in environmental cleaning and energy production processes due to the high oxidative/reductive activity it presents. In this work, there were established the most appropriate values of determined variables during the elaboration of boron doped TiO2 films on titanium, prepared by sol-gel method and deposited on the substrate by dip-coating, used as work electrode. It was evaluated the effect of the amount of water (0.3, 0.7 and 1.1 mL), the layers of the film (1, 2 and 3 layers) and the heating rate (1, 3 and 5 °C/min) on the material activity. The films were characterized by Field Emission Scanning Electron Microscopy, Raman Spectroscopy and Diffuse Reflectance Spectroscopy. The photoelectrocatalytic properties were studied by voltammetry measures under visible light. The results show that the final parameters that most affect the films activity are their thickness and uniformity, that are both modified by all the variables studied and that determine the transport of electrons. The conditions in which the best properties were obtained were 0.7 mL of water, 1 layer of film and 3°C/min as heating rate. Additionally, it was proved that doping with boron modify the films band-gap increasing the activity under visible light. The photoelectrocatalytic activity of the material was evaluated in the degradation of an organic compound (glycerol) achieving 25% of degradation in 2 hours. Bachelor
dc.description.degreelevelPregrado
dc.description.degreenameIngeniero Químico
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/33008
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicoquímicas
dc.publisher.programIngeniería Química
dc.publisher.schoolEscuela de Ingeniería Química
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.subjectPelículas B-Tio2/Ti
dc.subjectFotoelectrocatálisis
dc.subjectLuz Visible
dc.subjectTransporte De Electrones
dc.subjectGlicerol.
dc.subject.keywordB-Tio2/Ti Films
dc.subject.keywordPhotoelectrocatalysis
dc.subject.keywordVisible Light
dc.subject.keywordTransport Of Electrons
dc.subject.keywordGlycerol.
dc.titleSíntesis y caracterización de electrodos de b-tio2/ti para la oxidación fotoelectrocatalítica de glicerol bajo luz visible
dc.title.englishSynthesis and characterization of b-tio2/ti electrodes for photoelectrocatalytic oxidation of glycerol under visible light
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_7a1f
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
648.47 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
2.13 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
279.72 KB
Format:
Adobe Portable Document Format
Download
Collections
Ingeniería Química