Síntesis y evaluación de recubrimientos de mgf2 por conversión química sobre aleaciones de magnesio para la fabricación de implantes ortopédicos biodegradables de uso temporal

Simple item page
dc.contributor.advisorCoy Echeverría, Ana Emilse
dc.contributor.advisorViejo Abrante, Fernando
dc.contributor.authorCasanova Gómez, Paula Yolanda
dc.contributor.authorJaimes Corzo, Katherin Johana
dc.date.accessioned2024-03-03T19:28:01Z
dc.date.available2012
dc.date.available2024-03-03T19:28:01Z
dc.date.created2012
dc.date.issued2012
dc.description.abstractInvestigaciones recientes han postulado al magnesio como un candidato de uso potencial en la fabricación de implantes ortopédicos biodegradable de uso temporal gracias a su excelente biocompatibilidad y adecuadas características mecánicas. Sin embargo, en el proceso de degradación se genera una elevada evolución de hidrógeno cuya acumulación puede dar lugar a la necrosis de los tejidos circundantes, lo cual hace que su uso en este tipo de aplicaciones se vea reducida. Con objeto de evitar este inconveniente, en la actualidad una de las opciones consideradas es la síntesis de recubrimientos de características biodegradables que controlen el proceso de degradación del magnesio, de tal manera que el implante pueda mantener suficiente integridad mecánica durante el periodo de curación del tejido óseo dañado así como controlar la generación de hidrógeno. En el presente trabajo se seleccionaron las aleaciones comerciales Elektron 21 como objeto de estudio y la aleación AZ91D a modo comparativo, sobre las cuales se realizó un tratamiento por conversión química en soluciones acuosas con diferentes concentraciones de HF con el objetivo de obtener recubrimientos biodegradables de MgF2. Las muestras con y sin recubrimiento se evaluaron mediante ensayos gravimétricos y electroquímicos de polarización anódica en solución fisiológica simulada Hank, mientras que las pruebas de evolución de hidrógeno se realizaron en solución de NaCl 0,9% en peso. La caracterización del recubrimiento y de los productos de corrosión se llevó a cabo mediante microscopía electrónica de barrido (SEM-EDX) y difracción de rayos X (DRX). Los resultados obtenidos mostraron que los recubrimientos de MgF2 reducen de forma significativa la velocidad de corrosión así como la evolución de hidrógeno de las aleaciones estudiadas. El análisis de los productos resultantes de la degradación del recubrimiento demostró que estos eran ricos en oxígeno, fósforo y calcio, hecho que evidencia un potencial carácter bioactivo de las aleaciones recubiertas.
dc.description.abstractenglishMagnesium alloys have been recently considered as attractive candidates for the potential fabrication of temporary orthopedic implants, due to their excellent combination of biocompability and mechanical properties. Nevertheless, their degradation is accompanied by the hydrogen evolution which accumulation may originate necrosis of the surroundings tissues. In order to overcome this inconvenient, one of the options recently considered is the synthesis of biodegradable coatings, which can be able to control the magnesium degradation, so that the mechanical integrity of the implant may be maintained during the bone healing process. In the present work the commercial Elektron 21 and AZ91D (as reference) magnesium alloys were selected. Over both alloy MgF2 biodegradable coating was synthetized by immersion of the specimens in aqueous solutions with different proportions of HF up to 4% (vol.). The specimens were then evaluated by electrochemical and gravimetric test in Hank´s solution, while the hydrogen evolution test was carried out in 0.9 wt.% NaCl solution. Both the coating and the corrosion products resultant from the degradation process of the specimens were examined by scanning electron microscopy (SEM-EDX) and X-ray diffraction (XRD). The results showed that MgF2 coatings significantly reduced the corrosion rate of the magnesium alloys studied. The analysis of the corrosion products confirmed the presence of oxygen, phosphorous and calcium that suggests an bioactive character of the coated specimens.
dc.description.degreelevelPregrado
dc.description.degreenameIngeniero Químico
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/26659
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicoquímicas
dc.publisher.programIngeniería Química
dc.publisher.schoolEscuela de Ingeniería Química
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.subjectBioimplantes
dc.subjectRecubrimientos
dc.subjectAleaciones de magnesio
dc.subjectConversión química
dc.subject.keywordBioimplants
dc.subject.keywordCoatings
dc.subject.keywordMagnesium alloys
dc.subject.keywordChemistry conversion
dc.titleSíntesis y evaluación de recubrimientos de mgf2 por conversión química sobre aleaciones de magnesio para la fabricación de implantes ortopédicos biodegradables de uso temporal
dc.title.englishSynthesis and evaluation of mgf2 chemistry conversion coatings over magnesium alloys for the production of biodegradable implants for temporary use orthopedic
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_7a1f
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
1.35 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
4.17 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
1.18 MB
Format:
Adobe Portable Document Format
Download
Collections
Ingeniería Química