CORROSIÓN EN ACEROS AL CARBONO N-80 EN PROCESOS DE RECOBRO MEJORADO CON CATALIZADORES LIPOSOLUBLES.

Simple item page
dc.contributor.advisorPeña Ballesteros, Darío Yesid
dc.contributor.authorPaipa Gómez, Mery Saray
dc.contributor.authorSilva Torres, Danna Camila
dc.contributor.evaluatorCoy Echeverría, Ana Emilse
dc.contributor.evaluatorGalán Pinilla, Carlos Andrés
dc.date.accessioned2025-05-20T14:44:18Z
dc.date.available2025-05-20T14:44:18Z
dc.date.created2025-05-13
dc.date.issued2025-05-13
dc.description.abstractEl presente estudio evaluó la cinética de corrosión de cupones de acero API N-80Q expuesto a tres diferentes composiciones de crudos colombianos (A, B y C) mediante la técnica de acuatermólisis catalítica utilizando nafteno de hierro. Los ensayos se realizaron en un reactor Batch, a 270°C y 600 psi, con tiempos de 10 h, 30 h, 60 h, y 120 h de exposición, que simulan condiciones operativas. Además, para la limpieza de las piezas se usó la norma ASTM G1-03. La determinación de la velocidad de corrosión se realizó mediante la norma ASTM G31 12 donde se evidenció que la presencia del catalizador genera inicialmente una mayor oxidación (hasta 60 h) y después, una estabilización posiblemente generada por el aporte pasivo de magnetita (Fe3O4) y sulfuros (FeS en crudo C). Los resultados confirmaron que (a) la velocidad de corrosión se redujo de forma significativa después de 30 horas, alcanzando valores cercanos a 0 mpy a las 120 horas y (b) el crudo C mostró un comportamiento anómalo de ganancia de masa, que fue atribuida a la sinergia entre ácidos naftenicos y compuestos sulfurados. La caracterización morfológica y composicional por microscopia electrónica de barrido (SEM-EDS) mostró la formación de productos heterogéneos de corrosión (óxidos y sulfuros) sobre la superficie del acero con una distribución más homogénea en los ensayos catalíticos. El naftenato de hierro demostró potencial como inhibidor al promover la pasivación del metal, reduciendo la velocidad de corrosión en un 40-60% tras 100 h de exposición.
dc.description.abstractenglishThis study evaluated the corrosion kinetics of API N-80Q steel coupons exposed to three different compositions of Colombian crude oils (A, B and C) by means of the catalytic aquathermolysis technique using iron naphthene. The tests were carried out in a Batch reactor, at 270°C and 600 psi, with exposure times of 10 h, 30 h, 60 h, and 120 h, which simulate operating conditions. In addition, ASTM G1-03 was used for cleaning the parts. The determination of the corrosion rate was carried out using the ASTM G31-12 standard, where it was shown that the presence of the catalyst initially generates a higher oxidation (up to 60 h) and subsequently, a possible stabilization by the passive contribution of magnetite (Fe3O4) and sulfides (FeS in crude C). The results confirmed that (a) the corrosion rate was significantly reduced after 30 h, reaching values close to zero mpy at 120 h and (b) crude C showed an anomalous mass gain behavior, which was attributed to the synergy between naphthenic acids and sulfide compounds. Morphological and compositional characterization by scanning electron microscopy (SEM-EDS) showed the formation of heterogeneous corrosion products (oxides and sulfides) on the steel surface with a more homogeneous distribution in the catalytic tests. Iron naphthenate showed potential as an inhibitor by promoting metal passivation, reducing the corrosion rate by 40-60% after 100 h of exposure.
dc.description.degreelevelPregrado
dc.description.degreenameIngeniero Metalúrgico
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/45538
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingeníerias Fisicoquímicas
dc.publisher.programIngeniería Metalúrgica
dc.publisher.schoolEscuela de Ingeniería Metalúrgica y Ciencia de Materiales
dc.rightsinfo:eu-repo/semantics/openAccess
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.coarhttp://purl.org/coar/access_right/c_abf2
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAtribución-NoComercial-SinDerivadas 2.5 Colombia (CC BY-NC-ND 2.5 CO)
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/4.0/
dc.subjectCorrosión
dc.subjectAcero N-80Q
dc.subjectRecuperación mejorada
dc.subjectCatalizadores liposolubles
dc.subject.keywordN-80Q steel
dc.subject.keywordimproved recovery
dc.subject.keywordfat-soluble catalysts
dc.subject.keywordCorrosion
dc.titleCORROSIÓN EN ACEROS AL CARBONO N-80 EN PROCESOS DE RECOBRO MEJORADO CON CATALIZADORES LIPOSOLUBLES.
dc.title.englishCorrosion of n-80 steel in recovery processes enhanced with fat-soluble iron naphthenate catalysts
dc.type.coarhttp://purl.org/coar/resource_type/c_7a1f
dc.type.hasversionhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
169.63 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
104.43 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
993.43 KB
Format:
Adobe Portable Document Format
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
2.18 KB
Format:
Item-specific license agreed to upon submission
Description:
Download
Collections
Ingeniería Metalúrgica