dc.description.abstractEn el presente trabajo se evaluó la susceptibilidad del acero 1.25Cr 0.5Mo a presentar fragilidad por revenido; exponiendo el acero nuevo (Estado 1) a condiciones de temperatura, velocidad de enfriamiento y tiempos de sostenimiento críticos, mediante la aplicación de un tratamiento térmico de enfriamiento escalonado estándar (Estado 2), comúnmente utilizado para fomentar este mecanismo de daño. También se sometió a un tratamiento térmico de enfriamiento escalonado simulado (Estado 3), propuesto por los autores. El acero en sus tres estados fue caracterizado química, metalográfica y mecánicamente, con fines comparativos. Se les práctico el ensayo de impacto Charpy, obteniendo las curvas de transición dúctil frágil correspondientes. A partir de las correlaciones con el ensayo Charpy, se determinó la tenacidad a la fractura del acero 1.25Cr 0.5Mo, permitiendo comparar los resultados y evaluar si se presentó fragilización por revenido. Los resultados de la caracterización del material arrojaron valores muy similares para los diferentes estados del material, sin embargo aunque el tamaño de grano permaneció constante se apreció un leve aumento en la cantidad de precipitados en la matriz de los granos en el estado 3. De acuerdo al análisis químico se encontró que el acero presenta susceptibilidad a la fragilización por revenido, como se comprobó al realizar las curvas de transición obtenidas a partir del ensayo de impacto Charpy. Las curvas para el acero en estado 1 y 2, no presentan diferencias considerables, indicando que el tratamiento de enfriamiento escalonado estándar no induce fragilidad por revenido en este tipo de aceros. La curva para el acero en estado 3, presentó un desplazamiento hacia la derecha con respecto a las anteriores, indicando una reducción en la tenacidad del acero, por lo que se concluye que este tratamiento térmico propuesto por los autores si induce fragilidad por revenido en los aceros 1.25 Cr 0.5 Mo.
dc.description.abstractenglishThis work evaluates the susceptibility of 1.25Cr 0.5Mo steel to present temper embrittlement; exposing the new steel (State 1) to temperature conditions, cooling rates and step holding times, through the standard step cooling (State 2), commonly used to promote this damage mechanism. Also a simulated step cooling (State 3) was performed, created by the authors. The steel was characterized by chemist, metallography and mechanically to be compared between them. A Charpy impact test was performed to get the transitions curves and fracture toughness correlations for each state of the 1.25Cr 0.5Mo steel, allowing compare the results and evaluate if some temper embrittlement was presented. The results of characterizing the steel, gave very similar values on the different states of the steel, however even if the grain size does not change, a brief increasing of the precipitates on the matrix at the state 3 was noted. According to the chemical analysis, temper embrittlement susceptibility was found, as evidenced in the transition curves from the Charpy impact test. The transition curves for the states 1 and 2 do not show differences between them, proving that the standard step cooling was not able to reproduced temper embrittlement in this 1.25Cr 0.5Mo steels. The curve for the steel at the state 3 show a displacement to the right with respect to the previous, indicating a steel toughness reduction, concluding that this simulated steep cooling proposed by the authors is able to reproduce the temper embrittlement on 1.25Cr 0.5Mo steels.
dc.description.degreelevelPregrado
dc.description.degreenameIngeniero Metalúrgico
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/26828
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicoquímicas
dc.publisher.programIngeniería Metalúrgica
dc.publisher.schoolEscuela de Ingeniería Metalúrgica y Ciencia de Materiales
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.subjectTenacidad a la fractura
dc.subjectFragilización por revenido
dc.subjectAcero 1.25Cr 0.5Mo
dc.subjectCurva de transición dúctil frágil
dc.subjectTratamiento térmico de enfriamiento escalonado.
dc.subject.keywordFracture toughness
dc.subject.keywordTemper embrittlement
dc.subject.keyword1.25Cr 0.5Mo Steel
dc.subject.keywordDuctile brittle transition curve
dc.subject.keywordStep cooling.
dc.titleEvaluación de la susceptibilidad a la fragilidad por revenido del acero 1.25cr-0.5mo utilizado en equipos de plantas de procesos de Ecopetrol S.A. luego de la aplicación de ciclos de tratamiento térmico en intervalos de temperatura
dc.title.englishEvaluation of temper embrittlement susceptibility of 1.25 cr 0.5 mo steel used in equipment of one processing plant of Ecopetrol s.a. after the application of step cooling procedures in thermic intervals where this damage mechanism can be presented
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_7a1f
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
669.54 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
3.35 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
501.56 KB
Format:
Adobe Portable Document Format
Download
Collections
Ingeniería Metalúrgica