Evaluación preliminar de la influencia de un cemento álcali-activado en la respuesta  mecánica de materiales granulares marginales (MGM 3 & 9)

Rodríguez Ramírez, Carmen Cecilia; Moreno Saavedra, Fabian Andrés

Evaluación preliminar de la influencia de un cemento álcali-activado en la respuesta mecánica de materiales granulares marginales (MGM 3 & 9)

dc.contributor.advisor	Merchán Jaimes, Vladimir Ernesto
dc.contributor.advisor	Álvarez Lugo, Allex Eduardo
dc.contributor.author	Rodríguez Ramírez, Carmen Cecilia
dc.contributor.author	Moreno Saavedra, Fabian Andrés
dc.contributor.evaluator	Castañeda Pinzón, Eduardo Alberto
dc.contributor.evaluator	Cruz Hernandez, Ricardo Alfredo
dc.date.accessioned	2024-08-20T16:01:27Z
dc.date.available	2024-08-20T16:01:27Z
dc.date.created	2024-08-17
dc.date.embargoEnd	2029-08-17
dc.date.issued	2024-08-17
dc.description.abstract	En el presente proyecto de investigación se evalúa la viabilidad técnica del uso de un cemento álcali-activado (CAA)—generado a partir de escoria de alto horno—como estabilizante de dos materiales granulares marginales (MGM), en comparación con el uso de cemento Portland ordinario (CPO). Los materiales en estudio se denominan MGM-3 y MGM-9 y son analizados con partículas que pasan el tamiz No. 4 (4.75 mm) y porcentaje de finos del 18% y 24%, respectivamente (ambos con índice de plasticidad del 15%). Las dosificaciones de los cementantes son del 3%, 5%, y 7%. El material MGM-3 se analizó para dos tiempos de curado, 7 y 28 días, con dos réplicas para cada ensayo. En el caso del MGM-9, el análisis se realizó solo a 7 días, con una réplica. Los resultados indicaron que el uso de CPO como estabilizante produjo resultados superiores en comparación con la estabilización mediante el CAA evaluado aquí. Además, se determinó que el tiempo de curado influye de manera significativa en la resistencia de los materiales estabilizados, ya que a los 28 días se apreciaron incrementos hasta del 38% con el empleo de CPO, mientras que para CAA se obtuvo incrementos hasta del 86% utilizando un 3% o 5 % de este cementante. Cabe resaltar que con un 7% de CAA el incremento fue aún más notable, alcanzando hasta un 700% respecto a la resistencia a 7 días. Este aumento es un indicativo de la activación de la escoria con los químicos empleados; por lo tanto, es posible optimizar la dosificación y la activación del CAA mediante estudios futuros.
dc.description.abstractenglish	This research project evaluates the technical feasibility of using an alkali activated cement (AAC)—fabricated based on using blast furnace slag—as a stabilizer for two marginal granular materials (MGM) compared to ordinary Portland cement (OPC). The materials under study are termed as MGM-3 and MGM-9 and are analyzed with particles passing the No. 4 sieve (4.75 mm) and fines content of 18% and 24%, respectively (with a plasticity index of 15%). The cement dosages were 3%, 5%, and 7%. The MGM-3 material was analyzed for two curing times, 7 and 28 days, with two replicates for each test. In the case of MGM-9, the analysis was performed only at seven days, with one replicate. The results indicated that the use of OPC as a stabilizer produced superior results compared to the stabilization using the AAC evaluated here. In addition, it was determined that the curing time has a significant influence on the strength of the stabilized materials, since at 28 days, increases of up to 38% were observed with the use of CPO, while for AAC, increases of up to 86% were obtained using 3% or 5% of this cementitious agent. It should be noted that with 7% AAC the increase was even more notable, reaching up to 700% with respect to the 7-day strength. This increase is indicative of the activation of the slag with the chemicals used; therefore, it is possible to optimize the dosage and activation of the CAA through future studies.
dc.description.degreelevel	Pregrado
dc.description.degreename	Ingeniero Civil
dc.format.mimetype	application/pdf
dc.identifier.instname	Universidad Industrial de Santander
dc.identifier.reponame	Universidad Industrial de Santander
dc.identifier.repourl	https://noesis.uis.edu.co
dc.identifier.uri	https://noesis.uis.edu.co/handle/20.500.14071/43790
dc.language.iso	spa
dc.publisher	Universidad Industrial de Santander
dc.publisher.faculty	Facultad de Ingeníerias Fisicomecánicas
dc.publisher.program	Ingeniería Civil
dc.publisher.school	Escuela de Ingenieria Civil
dc.rights	info:eu-repo/semantics/embargoedAccess
dc.rights.accessrights	info:eu-repo/semantics/openAccess
dc.rights.coar	http://purl.org/coar/access_right/c_f1cf
dc.rights.creativecommons	Atribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.license	Atribución-NoComercial-SinDerivadas 2.5 Colombia (CC BY-NC-ND 2.5 CO)
dc.rights.uri	http://creativecommons.org/licenses/by-nc-nd/4.0/
dc.subject	Cemento álcali-activado
dc.subject	Cemento Portland
dc.subject	Material granular marginal
dc.subject	Estabilización de materiales
dc.subject	Compresión uniaxial
dc.subject	Tracción indirecta
dc.subject	Triaxial dinámico
dc.subject.keyword	Alkali-activated cement
dc.subject.keyword	Portland cement
dc.subject.keyword	Marginal granular material
dc.subject.keyword	Material stabilization
dc.subject.keyword	Uniaxial compression
dc.subject.keyword	Indirect tension
dc.subject.keyword	Dynamic triaxial
dc.title	Evaluación preliminar de la influencia de un cemento álcali-activado en la respuesta mecánica de materiales granulares marginales (MGM 3 & 9)
dc.title.english	Preliminary evaluation of the influence of an alkali-activated cement on the mechanical response of marginal granular materials (MGM 3 & 9)
dc.type.coar	http://purl.org/coar/resource_type/c_7a1f
dc.type.hasversion	http://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.local	Tesis/Trabajo de grado - Monografía - Pregrado