Evaluación no destructiva de concreto reforzado y adicionado con fibra expuesto a fuego

Simple item page
dc.contributor.advisorCruz Hernández, Ricardo Alfredo
dc.contributor.advisorQuintero Ortiz, Luz Amparo
dc.contributor.authorLópez De La Hoz, Maria Victoria
dc.contributor.authorSáenz Peñaloza, William Josmar
dc.date.accessioned2024-03-03T19:29:39Z
dc.date.available2012
dc.date.available2024-03-03T19:29:39Z
dc.date.created2012
dc.date.issued2012
dc.description.abstractLa velocidad de pulso ultrasónico es una técnica que durante los últimos años ha sido utilizada como un ensayo no destructivo para la inspección de materiales. En la presente investigación se evaluó mediante ensayos no destructivos, el concreto reforzado y adicionado con fibra sometido a fuego. Para esto se fabricaron 23 probetas en forma de paralelepípedos con dimensiones de 0.30x0.30x0.15 m, elaboradas con una relación Agua/Cemento de 0.6, a las cuales fue necesario introducir 3 termocuplas como sensores de temperatura a diferentes distancias de la cara de exposición, 3 de las probetas se elaboraron sin adición de fibra con el fin de conocer el comportamiento de la misma. Se realizaron ensayos de fuego a diferentes temperaturas y para cada ensayo se utilizaron 3 probetas, para la exposición a fuego se utilizo un horno y un programa desarrollado en Labview 8.5 que permitió el registro de las temperaturas internas de las probetas y el control de temperatura de la llama, mostrando las curvas de calentamiento en razón del tiempo de exposición para cada probeta. Los resultados obtenidos mostraron que a medida que aumenta la temperatura de exposición, los valores de velocidad de pulso ultrasónico y resistencia a la compresión disminuyen. Luego mediante técnicas de inspección visual se determinó que la fibra de polipropileno ayuda a disminuir el daño causado por el fuego, debido a que las 3 probetas sin fibra presentaron un mayor daño y registraron los menores valores de VPU y resistencia la compresión. Finalmente se realizó una relación entre la resistencia a la compresión y la velocidad de pulso ultrasónico donde se pudo observar que estos parámetros son directamente proporcionales y se ven afectados luego de la exposición a fuego.
dc.description.abstractenglishThe ultrasonic pulse velocity is a technique that in recent years has been used as a nondestructive testing for materials inspection. In this research was tested through non-destructive testing and added reinforced concrete fiber subjected to fire. A total of 23 test tubes were fabricated in the form of parallelepipeds with dimensions of 0.30x0.30x0.15 m, made with a water / cement ratio of 0.6, which was necessary to enter 3 thermocouples as temperature sensors at different distances from the face of exposure, 3 of the specimens were prepared without addition of fiber to know the behavior of the same. Fire tests were conducted at different temperatures and for each test 3 samples were used for exposure to fire a furnace and use a program developed in Labview 8.5 that allowed the recording of internal temperatures of the samples and the temperature control flame heating curves showing because of the exposure time for each specimen. The results showed that as the exposure temperature increases, the speed values ultrasound pulse and the compressive strength decreases. After visual inspection techniques was determined that the polypropylene fiber helps reduce the damage caused by fire, because the 3 samples without fiber damage and had higher values recorded under VPU and compression resistance. Finally a relationship between resistance to compression and velocity of ultrasonic pulse was conducted, and it was observed that these parameters are directly proportional and are unaffected after exposure to fire.
dc.description.degreelevelPregrado
dc.description.degreenameIngeniero Metalúrgico
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/26797
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicoquímicas
dc.publisher.programIngeniería Metalúrgica
dc.publisher.schoolEscuela de Ingeniería Metalúrgica y Ciencia de Materiales
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.titleEvaluación no destructiva de concreto reforzado y adicionado con fibra expuesto a fuego
dc.title.englishAssessing disruption of reinforced concrete and added fiber exposed to fire
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_7a1f
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
600.95 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
10.01 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
293.61 KB
Format:
Adobe Portable Document Format
Download
Collections
Ingeniería Metalúrgica