Evaluación del Desacoplamiento Químico de Polietilenos Entrecruzados XLPE usando Solventes en Estado Supercrítico.

Simple item page
dc.contributor.advisorRamírez Caballero, Gustavo Emilio
dc.contributor.advisorBravo Sanabria, Cesar Augusto
dc.contributor.advisorMartínez Ortega, Fernando
dc.contributor.authorAcuña Fernández, Zaira Alejandra
dc.contributor.authorBarajas Reyes, Maria Andrea
dc.contributor.evaluatorAvellaneda Vargas, Fredy Augusto
dc.contributor.evaluatorGuerrero Amaya, Hernando
dc.date.accessioned2022-11-04T20:39:06Z
dc.date.available2022-11-04T20:39:06Z
dc.date.created2022-11-03
dc.date.issued2022-11-03
dc.description.abstractTítulo: Evaluación del desacoplamiento químico de polietilenos entrecruzados XLPE usando solventes en estado supercrítico Autor: Maria Andrea Barajas Reyes, Zaira Alejandra Acuña Fernández Palabras clave: Entrecruzamiento, Desacoplamiento, Estado Supercrítico, Contenido en Gel, Reactor Batch, XLPE, LDPE. Descripción: Este trabajo plantea un tratamiento alternativo para el Scrap de cables eléctricos tipo polietilenos entrecruzados XLPE usando solventes en estado supercrítico. El tratamiento consistió en una reacción llevada a cabo en un reactor batch a 250°C durante 30 minutos, en la cual se evaluaron dos condiciones críticas: el efecto de diferentes solventes en estado supercrítico y el tamaño de partícula del XLPE. Los solventes que se emplearon fueron: isopropanol, etanol y acetona y los tamaños de partícula que se emplearon fueron: compacto o sin reducción de tamaño, que corresponde a una unidad cilíndrica extraída directamente del cable eléctrico y granulado, que se obtiene a partir de una fuerza de cizalla sobre el cable. Los resultados indican que las condiciones de reacción fueron suficientes para el desentrecruzamiento del material polimérico, pasando de un contenido en gel inicial de 50.56% a porcentajes en gel de aproximadamente 12% para las muestras granuladas con etanol supercrítico como solvente, las cuales fueron las condiciones que obtuvieron el mayor desempeño sobre el desacoplamiento del XPLE. De igual forma se estudiaron las características fisicoquímicas implicadas en el desentrecruzamiento del material mediante espectroscopia infrarroja ATR, difracción de rayos X, TGA y DSC. Por otro lado, el estudio preliminar de la cinética permitió evidenciar una tendencia de disminución lineal de concentración de gel a medida que el tiempo de reacción aumenta siguiendo un comportamiento que encaja con un modelo de reacción de primer orden, mediante el cual, finalmente se obtuvo que la constante de velocidad de reacción de desacoplamiento a 250°C es 0.063 min-1.
dc.description.abstractenglishTitle: Evaluation of the chemical de-crosslinking of the crosslinked polyethylene XLPE using solvents in supercritical state. Author: Maria Andrea Barajas Reyes, Zaira Alejandra Acuña Fernández Key words: Crosslinking, De-crosslinking, Supercritical State, Gel Content, Batch Reactor, XLPE, LDPE. Description: This work proposes an alternative treatment for the Scrap of electrical cables type cross-linked polyethylene XLPE using solvents in supercritical state. The treatment consisted of a reaction carried out in a batch reactor at 250°C for 30 minutes, in which, two critical conditions were evaluated: the effect of different reagents (solvents) in supercritical state and the particle size of the XLPE. The solvents that were used were: isopropanol, ethanol and acetone and the particle sizes that were used were: compact or without size reduction, which corresponds to a cylindrical unit extracted directly from the electric cable and granulated, which is obtained from scratched of cable. The results indicate that the synthesis conditions were sufficient for the decrosslinking of the polymeric material, going from an initial gel content of 50.56% to gel percentages of approximately 12% for the granulated samples with supercritical ethanol as solvent, which were the conditions that obtained the best performance on the decoupling of the XPLE. In the same way, the physicochemical characteristics involved in the decrosslinking of the material were studied by means of ATR infrared spectroscopy, X-ray diffraction, TGA and DSC. On the other hand, the preliminary study of the kinetics allowed to show a trend of linear decrease in gel concentration as the reaction time increases, following a behavior that fits with a first-order reaction model, by means of which, finally, was found that the decoupling reaction rate constant at 250°C is 0.063 min-1.
dc.description.degreelevelPregrado
dc.description.degreenameIngeniero Químico
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/11915
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingeníerias Fisicoquímicas
dc.publisher.programIngeniería Química
dc.publisher.schoolEscuela de Ingeniería Química
dc.rightsinfo:eu-repo/semantics/openAccess
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.coarhttp://purl.org/coar/access_right/c_abf2
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/4.0/
dc.subjectEntrecruzamiento
dc.subjectDesacoplamiento
dc.subjectEstado Supercrítico
dc.subjectContenido en Gel
dc.subjectReactor Batch
dc.subjectXLPE
dc.subjectLDPE
dc.subject.keywordCrosslinking
dc.subject.keywordDe-crosslinking
dc.subject.keywordSupercritical State
dc.subject.keywordGel Content
dc.subject.keywordBatch Reactor
dc.subject.keywordXLPE
dc.subject.keywordLDPE
dc.titleEvaluación del Desacoplamiento Químico de Polietilenos Entrecruzados XLPE usando Solventes en Estado Supercrítico.
dc.title.englishEvaluation of the chemical de-crosslinking of the crosslinked polyethylene XLPE using solvents in supercritical state.
dc.type.coarhttp://purl.org/coar/resource_type/c_7a1f
dc.type.hasversionhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
dspace.entity.type
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Documento.pdf
Size:
1.58 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Carta de autorización .pdf
Size:
152.69 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
88.99 KB
Format:
Adobe Portable Document Format
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
2.18 KB
Format:
Item-specific license agreed to upon submission
Description:
Download
Collections
Ingeniería Química