Disolucion de la ilmenita (fetio3) proveniente de arenas negras, inducida por molienda de alta energia
| dc.contributor.advisor | Neira Arenas, Gustavo | |
| dc.contributor.author | Gutierrez Perez, Denis Natalia | |
| dc.date.accessioned | 2024-03-03T04:39:41Z | |
| dc.date.available | 2004 | |
| dc.date.available | 2024-03-03T04:39:41Z | |
| dc.date.created | 2004 | |
| dc.date.issued | 2004 | |
| dc.description.abstract | Muestras de arenas negras concentradas fueron molidas por varios tiempos (10, 20, 40 y 100) en un molino Attritor, y lixiviadas en solución de acido sulfúrico al 50% a 100±5°C en autoclave y a 60±5°C en vasos de precipitados con agitación. Los sólidos residuales (colas) de lixiviacion fueron caracterizadas por difracción de rayos x, y las soluciones de lixiviacion fueron analizadas para hierro y titanio mediante espectrofotometría de absorción atómica. Adicionalmente, se aplicó análisis de imagines a los sólidos antes y después de la molienda para determinar área superficial, redondez y factor de forma. Mediante los resultados se comprobó que la molienda mecánica de alta energía del mineral aumenta la disolución de ilmenita y posiblemente de otros minerales presentes en el concentrado, principalmente óxidos de hierro. Se encontró que después de una molienda de 10 horas, el 86,71% de ilmenita fue disuelta durante su lixiviacion en autoclave, lo cual representa un aumento en su disolución del 80% con relación al mineral sin molienda mecánica. La disolución del mineral en vasos de precipitados también aumentó, pero no al mismo nivel que cuando la lixiviacion se llevó a cabo en autoclave. Tiempos de molienda superiores a 10 horas no mostraron un aumento progresivo de la disolución debido probablemente a algunas posibles transformaciones del mineral y a cambios en su comportamiento a la lixiviacion. En el aspecto físico, el análisis de imagines mostró que durante la molienda las partículas son sometidas más a fracturamiento constante que a reducción de tamaño por fricción, y evidencia una estrecha relación entre la molienda mecánica del mineral y su comportamiento a la lixiviacion. | |
| dc.description.abstractenglish | Samples of concentrated black sands were ball milled for different periods of time (10, 20, 40 and 100 hours) in an Attritor mill, and then were leached in a 50% v/v sulphuric acid solution at 100 ± 5 °C in autoclave and at 60 ± 5 °C in stirred vickers. The residual leaching solids (tailings) were characterized by X-Ray Diffraction, and the leach solutions were analized for Fe and Ti by atomic absorption spectrophotometry. Additionally, image analysis were applied to the solids in order to determine their surface area, esphericity and shape factor. It was proved that the high energy milling of the mineral increases the dissolution of ilmenite and possibly that of other minerals, mainly iron oxides. It was found that, after a milling of ten hours, 86.71 % of ilmenite was dissolved during its leaching in autoclave. This represents an increase in dissolution of 80 % in relation to the non-milled ore. The dissolution in beakers also showed an increase, though not at the same level as the dissolution in autoclave. Milling times higher than 10 hours did not show any progressive increase in dissolution, possibly due to possible transformations of the mineral, and changes of its leaching behaviour. In relation to physical aspects, immage analysis showed that on milling, particles are subjected to constant fracturing, rather than size reduction by wearing, and there was evidence that leaching behaviour is closely related to high energy mill balling of the ore. | |
| dc.description.degreelevel | Pregrado | |
| dc.description.degreename | Ingeniero Metalúrgico | |
| dc.format.mimetype | application/pdf | |
| dc.identifier.instname | Universidad Industrial de Santander | |
| dc.identifier.reponame | Universidad Industrial de Santander | |
| dc.identifier.repourl | https://noesis.uis.edu.co | |
| dc.identifier.uri | https://noesis.uis.edu.co/handle/20.500.14071/16538 | |
| dc.language.iso | spa | |
| dc.publisher | Universidad Industrial de Santander | |
| dc.publisher.faculty | Facultad de Ingenierías Fisicoquímicas | |
| dc.publisher.program | Ingeniería Metalúrgica | |
| dc.publisher.school | Escuela de Ingeniería Metalúrgica y Ciencia de Materiales | |
| dc.rights | http://creativecommons.org/licenses/by/4.0/ | |
| dc.rights.accessrights | info:eu-repo/semantics/openAccess | |
| dc.rights.creativecommons | Atribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0) | |
| dc.rights.license | Attribution-NonCommercial 4.0 International (CC BY-NC 4.0) | |
| dc.rights.uri | http://creativecommons.org/licenses/by-nc/4.0 | |
| dc.subject | Lixiviación | |
| dc.subject | Ilmenita | |
| dc.subject | Molienda de alta energía | |
| dc.subject | Arenas negras. | |
| dc.subject.keyword | Leaching | |
| dc.subject.keyword | Ilmenite | |
| dc.subject.keyword | High energy ball milling | |
| dc.subject.keyword | Black sands. | |
| dc.title | Disolucion de la ilmenita (fetio3) proveniente de arenas negras, inducida por molienda de alta energia | |
| dc.title.english | Dissolution of ilmenite (fetio3) coming of sands deposit, induced by high energy ball milling | |