Evaluación de la respuesta mecánica de un material granular marginal (MGM-1) estabilizado con un cemento álcali-activado obtenido a partir de la trituración de escoria de alto horno para uso como capa estructural en vías terciarias.

Cuervo Delgado, Víctor Jerónimo

Evaluación de la respuesta mecánica de un material granular marginal (MGM-1) estabilizado con un cemento álcali-activado obtenido a partir de la trituración de escoria de alto horno para uso como capa estructural en vías terciarias.

dc.contributor.advisor	Álvarez Lugo, Allex Eduardo
dc.contributor.advisor	López Parra, Jhonatan Steevens
dc.contributor.author	Cuervo Delgado, Víctor Jerónimo
dc.contributor.evaluator	RONDON, JOSE ALBERTO
dc.contributor.evaluator	TORRADO GOMEZ, LUZ MARINA
dc.date.accessioned	2025-08-15T16:24:06Z
dc.date.available	2025-08-15T16:24:06Z
dc.date.created	2025-08-14
dc.date.embargoEnd	2030-08-14
dc.date.issued	2025-06-14
dc.description.abstract	Se evaluó el comportamiento mecánico de un MGM (MGM-1) estabilizado con un cemento álcali-activado (CAA), producido a partir de escoria de alto horno triturada. El objetivo de este trabajo se centra en realizar un primer análisis para establecer la viabilidad del material estabilizado como capa estructural en vías terciarias en Colombia. Para alcanzar el objetivo, se diseñaron mezclas de MGM-1 con diferentes contenidos de CAA (0%, 3%, 5% y 7%) y se sometieron a procesos de curado de 7 y 28 días. Estas mezclas fueron sometidas a ensayos de laboratorio, incluyendo resistencia a la compresión inconfinada (RCI), resistencia a la tracción indirecta (RTI), y módulo resiliente (MR), para medir su resistencia y rigidez bajo cargas cíclicas. Los resultados mostraron que el aumento en el porcentaje de CAA y los tiempos prolongados de curado generan una mejora progresiva en las propiedades mecánicas, particularmente en la resistencia a la compresión y la tracción indirecta, alcanzando un máximo de 0,664 MPa en RCI con un porcentaje de CAA de 7% y tiempo de curado de 28 días; sin embargo, este valor no cumple con los requisitos mínimos de materiales granulares tratados con cemento para ser utilizado como capa estructural en vías terciarias. Asimismo, los ensayos dinámicos revelaron que, bajo condiciones de confinamiento y cargas repetitivas, las mezclas con un 7% de CAA y 28 días de curado mostraron un incremento significativo en la rigidez, mientras que para curados cortos (7 días) el mejor desempeño se encontró en las mezclas con 5% de CAA. El estudio también destacó la importancia de establecer correlaciones preliminares entre los resultados de los ensayos de RCI y MR, dado que los ensayos dinámicos presentan costos operativos mucho mayores. Aunque el uso de CAA contribuye a mejorar la resistencia del MGM-1, en las proporciones ensayadas no es suficiente para cumplir los estándares estructurales exigidos, sugiriéndose investigaciones adicionales para mejorar las propiedades del material granular estabilizado y maximizar su desempeño.
dc.description.abstractenglish	This study evaluated the mechanical behavior of an MGM (MGM-1) stabilized with an alkali-activated cement (AAC). MGM-1 mixtures were designed with varying AAC contents (0%, 3%, 5% and 7%) and subjected to curing periods of 7 and 28 days. Laboratory tests, including unconfined compressive strength (UCS), indirect tensile strength (ITS), and resilient modulus (MR), were conducted to evaluate the strength and stiffness under cyclic loading. Results showed that increasing AAC content and longer curing periods progressively improved mechanical properties, particularly compressive and tensile strength, reaching a maximum UCS of 0.664 MPa with 7% AAC and 28 days of curing. However, this value does not meet the minimum requirements for cement-treated granular materials to serve as structural layers in low-volume roads. Dynamic tests further revealed that, under confined conditions and repeated loading, mixtures with 7% AAC and 28 days of curing exhibited significant stiffness gains. In contrast, for shorter curing times (7 days), the best performance was observed in mixtures with 5% AAC. The study also highlighted the importance of establishing preliminary correlations between UCS and MR results, given the high operational costs of dynamic triaxial tests. Although AAC improves the strength of MGM-1, at the tested proportions, it remains insufficient to meet the required structural standards, indicating the need for further research to enhance the response of the stabilized materials.
dc.description.degreelevel	Pregrado
dc.description.degreename	Ingeniero Civil
dc.format.mimetype	application/pdf
dc.identifier.instname	Universidad Industrial de Santander
dc.identifier.reponame	Universidad Industrial de Santander
dc.identifier.repourl	https://noesis.uis.edu.co
dc.identifier.uri	https://noesis.uis.edu.co/handle/20.500.14071/45895
dc.language.iso	spa
dc.publisher	Universidad Industrial de Santander
dc.publisher.faculty	Facultad de Ingeníerias Fisicomecánicas
dc.publisher.program	Ingeniería Civil
dc.publisher.school	Escuela de Ingenieria Civil
dc.rights.accessrights	info:eu-repo/semantics/openAccess
dc.rights.coar	http://purl.org/coar/access_right/c_abf2
dc.rights.creativecommons	Atribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.license	Atribución-NoComercial-SinDerivadas 2.5 Colombia (CC BY-NC-ND 2.5 CO)
dc.rights.uri	http://creativecommons.org/licenses/by-nc-nd/4.0/
dc.subject	Cemento álcali-activado
dc.subject	MGM
dc.subject	escoria de alto horno
dc.subject	módulo resiliente
dc.subject	vías terciarias
dc.subject.keyword	Alkali-activated cement
dc.subject.keyword	marginal granular material
dc.subject.keyword	ground granulated blast furnace slag
dc.subject.keyword	resilient modulus
dc.subject.keyword	low-volume roads
dc.title	Evaluación de la respuesta mecánica de un material granular marginal (MGM-1) estabilizado con un cemento álcali-activado obtenido a partir de la trituración de escoria de alto horno para uso como capa estructural en vías terciarias.
dc.title.english	Evaluation of the Mechanical Response of a Marginal Granular Material (MGM-1) Stabilized with an Alkali-Activated Cement Derived from Ground Granulated Blast Furnace Slag for Use as a Structural Layer in Tertiary Road
dc.type.coar	http://purl.org/coar/resource_type/c_7a1f
dc.type.hasversion	http://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.local	Tesis/Trabajo de grado - Monografía - Pregrado