dc.contributor.advisorLasprilla Álvarez, María del Carmen
dc.contributor.advisorFrejich, Jaime
dc.contributor.advisorOliveira, Iván de
dc.contributor.authorJerez Martínez, Vladimir Albeiro
dc.date.accessioned2024-03-03T18:47:58Z
dc.date.available2011
dc.date.available2024-03-03T18:47:58Z
dc.date.created2011
dc.date.issued2011
dc.description.abstractSe reporta la grabación de un holograma de transmisión en LiNbO3:Fe con máxima modulación del índice de refracción. Se utilizaron procesos simultáneos de grabación/compensación a 120°C, en un arreglo especialmente diseñado. Este método ha demostrado ser reproducible y ajustarse bien al modelo teórico. El análisis del proceso de grabación mostró que la saturación del material se alcanzó de manera que se obtuvo el máximo posible en modulación del índice de refracción. A partir de comparación de procesos teóricos y experimentales de grabación/compensación se determinaron los parámetros del material (tiempo de relajación dieléctrica =15min, saturación del campo de carga = 18.8 Kv/cm, y la relación campo fotovoltaico/saturación =0.80). La arreglo independiente y su valor real calculado teniendo en cuenta la divergencia del haz. El buen funcionamiento del filtro óptico de Bragg, se caracterizó con la medida de su selectividad angular (aproximadamente 1,2mrad) y espectral (aproximadamente 0.1nm), en la longitud de onda del haz 633nm. Se demostró que la grabación óptica en titano-selenitas Bi12TiO20(BTO) involucra electrones, iones y agujeros, dependiendo de las condiciones experimentales. La grabación y borrado del holograma a una temperatura mayor que la ambiental se llevaron a cabo en el cristal sin dopar, y se observó la presencia de un holograma fotosensible rápido de base electrónica y una compensación menor de naturaleza no fotosensible, responsable del holograma fijo en BTO y probablemente de base en iones H+. La rejilla fija mostró eficiencia de difracción y energía de activación 0,85±0,05eV. También se detectó un efecto fotocrómico fuerte inducido por luz (oscura, infrarroja), dicho efecto debe tenerse en cuenta para la medición de la eficiencia de difracción. Por primera vez se demuestra que los agujeros participan en el proceso de grabación óptica cuando son fotoexcitados selectivamente con infrarrojo.
dc.description.abstractenglishWe report the recording of a fixed good quality transmission hologram in LiNbO3:Fe with maximum index-of-refraction modulation using the simultaneous recording/compensation process at 120°C in a specially designed setup with =514.5 nm. This process was shown to be reproducible and in good agreement with an already reported theoretical model. The analysis of this recording process showed that material saturation was reached so that the maximum possible fixed index-of-refraction modulation was achieved. From the comparison of theoretical and experimental recording/compensation process data some material parameters (dielectric relaxation time =15 min, saturation space-charge field Eq=18.8 kV/cm, and photovoltaic-to-saturation field ratio Eph/Eq=0.80) were determined. The diffraction efficiency of this grating was measured using ( =633 nm) probe laser beam in an independent setup and its actual value computed, taking into account the angular divergence of the probe beam. The good grating performance as an optical Bragg filter was experimentally characterized by independently measuring its angular (approximately 1.2 mrad) and spectral (approximately 0.1 nm) selectivity, both at the probe beam wavelength of 633 nm. We show that optical recording in undoped photorefractive titanosillenite Bi12TiO20 (BTO) crystals involve electrons, holes and ions, depending on the experimental conditions. Holographic recording and erasure at higher than room temperature was carried out on an undoped crystal sample, showing the presence of a fast photosensitive electron-based hologram and a slower compensating one of non photosensitive nature that is responsible for hologram fixing in BTO and is likely to be based on H+ ions. The fixed grating showed a diffraction efficiency 0.002 and a characteristic activation energy of 0.85±0.05 eV. A strong light-induced (darkening) photochromic effect was also detected, that had to be accounted on for diffraction efficiency measurement. Holes are also shown to participate in the optical recording process when selectively photoexcited with infra-red light.
dc.description.degreelevelDoctorado
dc.description.degreenameDoctor en Ciencias Naturales
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/26059
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ciencias
dc.publisher.programDoctorado en Ciencias Naturales
dc.publisher.schoolEscuela de Física
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.subjectFijado de hologramas
dc.subjectLiNbO3:Fe
dc.subjectBi12TiO20
dc.subjectModulación del índice de refracción
dc.subject.keywordFixed holograms
dc.subject.keywordLiNbO3:Fe
dc.subject.keywordBi12TiO20
dc.subject.keywordIndex-of-refraction modulation
dc.titleGrabado de hologramas foto refractivos a alta temperatura
dc.title.englishFixed holograms photorefractive at high temperature
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_db06
dc.type.localTesis/Trabajo de grado - Monografía - Doctorado
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
248.67 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
2.22 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
93.09 KB
Format:
Adobe Portable Document Format
Download
Collections
Doctorado en Ciencias Naturales