Activación con molienda mecánica como pretratamiento en la cianuración de minerales refractarios de oro
| dc.contributor.advisor | Neira Arenas, Gustavo | |
| dc.contributor.author | Delgado Ramírez, Oscar Iván | |
| dc.contributor.author | Mendoza Prada, Alvaro Alexis | |
| dc.date.accessioned | 2024-03-03T16:10:12Z | |
| dc.date.available | 2006 | |
| dc.date.available | 2024-03-03T16:10:12Z | |
| dc.date.created | 2006 | |
| dc.date.issued | 2006 | |
| dc.description.abstract | Muestras de mineral refractario de oro concentrado (36g Au/Ton mineral) fueron sometidas a activación mecánica por varios tiempos (10, 20, y 40 horas) y diferente pH en un molino Attritor, y lixiviadas durante 48 horas mediante cianuración convencional con agitación constante, tomándose alícuotas a través del tiempo. Las soluciones de lixiviación fueron analizadas para la determinación de oro mediante espectrofotometría de absorción atómica. Adicionalmente, se aplicó difracción de rayos X, espectroscopia de infrarrojo, termogravimetría y análisis por fotosedimentación a los sólidos antes y después de la molienda para determinar los efectos de ésta sobre el mineral. Mediante los resultados se comprobó que la molienda mecánica de alta energía del mineral aumenta significativamente la disolución de oro, debido muy posiblemente al aumento de la reactividad química. Se encontró que después de una molienda de 10 horas, con adición de cal y 48 horas de lixiviación, el 69,85 de oro fue disuelto, lo cual representa un aumento en su disolución de aproximadamente del 30% con relación al mineral sin molienda mecánica. Tiempos de molienda superiores a 10 horas no mostraron un aumento efectivo de la disolución debido probablemente a algunas posibles transformaciones de las especies minerales, liberación de elementos cianicidas, transformación o pasivación de los minerales contenedores de oro, efectos granulométricos y/o cambios en su comportamiento a la lixiviación. Así mismo, los análisis de DRX, IR, termogravimetría y fotosedimentación, evidenciaron importantes efectos de la molienda mecánica, tales como la disminución progresiva del tamaño de partícula y la amorfización, inducción de transformaciones, desaparición de fases y distorsión de las redes cristalinas, entre otros. | |
| dc.description.abstractenglish | Concentrate refractory gold ore samples (36 g Au/Ton) were mechanically activated by milling in a attritor mill for different periods of time (10, 20 and 40 hours) and pH, and then leached for 48 hours by conventional leaching at constant stirring, taking aliquots along time. The leaching solutions were analyzed for gold by Atomic Absorption Spectrophotometry. Additionally, the solid particles before and after milling were examined by XRD, IR analysis, Thermogravimetry and Photosettling analysis, to determine the effects of activation on the ore. The results showed that high energy mechanicall milling of the ore increases significantly the dissolution of gold, probably due to the increase in chemical reactivity. It was found that after 10 hours milling, in the presence of lime and 48 hours leaching, 69,85% of gold was dissolved, which represents an increase of approximately 30% in comparison to the ore without milling. Periods of time higher than 10 hours milling did not show effective increases in gold dissolution, probably due to some possible transformations of mineral species, release of cyanide-consuming elements, transformation or pasivación of gold-containing minerals, granulometric effects and/or changes of behaviour during leaching. Moreover, the results of XRD, IR, TG and Photosetting analysis showed important effects of the milling, such as gradual decrease of particle size, amorphization, induced transformation, phase disappearance and lattice distorsion, amongst others. | |
| dc.description.degreelevel | Pregrado | |
| dc.description.degreename | Ingeniero Metalúrgico | |
| dc.format.mimetype | application/pdf | |
| dc.identifier.instname | Universidad Industrial de Santander | |
| dc.identifier.reponame | Universidad Industrial de Santander | |
| dc.identifier.repourl | https://noesis.uis.edu.co | |
| dc.identifier.uri | https://noesis.uis.edu.co/handle/20.500.14071/18813 | |
| dc.language.iso | spa | |
| dc.publisher | Universidad Industrial de Santander | |
| dc.publisher.faculty | Facultad de Ingenierías Fisicoquímicas | |
| dc.publisher.program | Ingeniería Metalúrgica | |
| dc.publisher.school | Escuela de Ingeniería Metalúrgica y Ciencia de Materiales | |
| dc.rights | http://creativecommons.org/licenses/by/4.0/ | |
| dc.rights.accessrights | info:eu-repo/semantics/openAccess | |
| dc.rights.creativecommons | Atribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0) | |
| dc.rights.license | Attribution-NonCommercial 4.0 International (CC BY-NC 4.0) | |
| dc.rights.uri | http://creativecommons.org/licenses/by-nc/4.0 | |
| dc.subject | Molienda de alta energía | |
| dc.subject | Activación mecánica | |
| dc.subject | Lixiviación de diagnóstico | |
| dc.subject | Minerales refractarios de oro. | |
| dc.subject.keyword | High energy ball milling | |
| dc.subject.keyword | Mechanical activation | |
| dc.subject.keyword | Diagnostic leaching | |
| dc.subject.keyword | Refractory gold ore | |
| dc.title | Activación con molienda mecánica como pretratamiento en la cianuración de minerales refractarios de oro | |
| dc.title.english | Mechanical milling activation as a pre-treatment for the cyanadation of refractory gold ore | |
| dc.type.coar | http://purl.org/coar/version/c_b1a7d7d4d402bcce | |
| dc.type.hasversion | http://purl.org/coar/resource_type/c_7a1f | |
| dc.type.local | Tesis/Trabajo de grado - Monografía - Pregrado |