Desarrollo de cerámicos refractarios silico-aluminosos a partir de arcillas caoliniticas de Barichara (Santander)

Simple item page
dc.contributor.advisorCórdoba Tuta, Elcy María
dc.contributor.authorPérez Ayala, Greysi Zulay
dc.contributor.authorVargas Rodríguez, Yuly Carolina
dc.date.accessioned2024-03-03T17:32:34Z
dc.date.available2009
dc.date.available2024-03-03T17:32:34Z
dc.date.created2009
dc.date.issued2009
dc.description.abstractEl presente proyecto estudió el beneficio de dos arcillas provenientes de Barichara Santander, denominadas por los artesanos de la región como cascajo y negra, con el fin de utilizarlas en la fabricación de refractarios sílicoaluminosos. El proceso de beneficio se llevó a cabo mediante operaciones metalúrgicas de tamizaje en húmedo, sedimentación, concentración magnética y lixiviación ácida inversa, mejorándose la calidad de las arcillas al eliminar algunas de sus impurezas e incrementando el %Al2O3 presente; y una vez selecciona la arcilla de mayor calidad, se empleó en el estudio de obtención de refractarios compuestos de arcilla-chamota bajo diferentes concentraciones y temperaturas. La chamota fue preparada por quemado de la arcilla beneficiada a 1300°C, y clasificada en rangos de tamaño de partícula de 100 µm a 2 mm. Se estudió la fabricación de los refractarios con diferentes mezclas arcillas/chamota, moldeando las pastas cerámicas bajo presión; posteriormente secadas al ambiente y en estufa entre 50 y 100ºC. Finalmente se sinterizaron los cerámicos entre 1200 y 1400ºC, en horno eléctrico bajo atmósfera oxidante. Los cerámicos obtenidos fueron caracterizados empleando técnicas de análisis mineralógico por Difracción de Rayos X (DRX) y Fluorescencia de Rayos X (FRX); microestructura por microscopía electrónica de barrido (SEM); densidad y porosidad aparente por método de Arquímedes; punto de ablandamiento por método de conos pirométricos, estabilidad térmica por ATD-TGA; resistencia a la flexión en frió; según norma ICONTEC 682 y resistencia al choque térmico según norma ICONTEC 1 432. Teniendo en cuenta los resultados, se seleccionó el cascajo para fabricar los cerámicos, por su reducción de Fe y aumento de Al2O3 de 97.5% y 73.39% respectivamente. Se determinó que las mejores condiciones para fabricar los refractarios, son: mezcla de 20%chamota-80%arcilla, sinterizada por 2 horas a 1300ºC. Finalmente se concluye que es posible desarrollar refractarios arcilla-chamota, para usos que no excedan los 1600ºC.1
dc.description.abstractenglishThis project studied the benefit of two clay which come from Barichara (Santander). They were designated by the region artisans as fiCascajofl and fiNegrafl to use them in the manufacture of aluminium silicate refractories. The process of benefiting was carried out by metallurgy operations of sifting in wet, sedimentation, magnetic concentration, and reversed acid lixiviation, getting better the quality of clay by disposing of some of their impurity and increasing the % Al2O3 present; and once the clay of the highest quality is selected, it was used in the study of obtaining composed refractories of chamotte-clay under different concentrations and temperatures. The chamotte was prepared by burning the benefited clay to 1300ºC, and it was classified in levels of particle size from 100 µm to 2 mm. It was studied the manufacture of refractories with different mixtures of clay-chamotte, molding the ceramic paste under pressure; later dried by the exposure to the environment, and in a stove between 50 and 100ºC. Finally, the ceramics were sintered between 1200 and 1400ºC in an electric kiln under an oxidizing atmosphere. The obtained, ceramics were characterized by using mineralogic analysis techniques by the difractioning of x-rays (DXR), and the fluorescence of x-rays (FRX); the micro-structure by sweeping electronic microscopy (SEM); apparent density and porosity by the Arquimedes method; softening point by the pirométrico cone method, thermic stability by ATDTGA; resistance to the cold bending; according to the ICONTEC 682 norm, and resistance to the thermic shock according to the ICONTEC 1432 norm. By taking into account the results, it was selected the Cascajo to fabricate the ceramics by its reduction of Fe and the increasing of Al2O3 of 97.5% and 73.39% respectively. It was determined that the best conditions to fabricate the refractories are: the mixture of 20% chamotte-80% clay sintered by two hours of exposure to 1300ºC. Finally, it is concluded that it is possible to develop clay-chamotte refractories, for uses that do not exceed 1600ºC.
dc.description.degreelevelPregrado
dc.description.degreenameIngeniero Metalúrgico
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/22317
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicoquímicas
dc.publisher.programIngeniería Metalúrgica
dc.publisher.schoolEscuela de Ingeniería Metalúrgica y Ciencia de Materiales
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.subjectArcillas
dc.subjectCaolinita
dc.subjectSinterización
dc.subjectRefractarios
dc.subjectChamota
dc.subjectMullita.
dc.subject.keywordClay
dc.subject.keywordKaolinite
dc.subject.keywordSintering
dc.subject.keywordRefractories
dc.subject.keywordChamotte
dc.titleDesarrollo de cerámicos refractarios silico-aluminosos a partir de arcillas caoliniticas de Barichara (Santander)
dc.title.englishDevelopment of refractory aluminium silicate ceramics from kaolinites clay from barichara (santander)
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_7a1f
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
652.3 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
4.5 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
848.84 KB
Format:
Adobe Portable Document Format
Download
Collections
Ingeniería Metalúrgica