Uso de la escoria de procesos metalúrgicos como agregado del concreto para la fabricación de elementos de construcción no estructurales

Simple item page
dc.contributor.advisorCruz Hernández, Ricardo Alfredo
dc.contributor.authorPérez Bustos, Ludwing
dc.date.accessioned2024-03-03T20:15:18Z
dc.date.available2013
dc.date.available2024-03-03T20:15:18Z
dc.date.created2013
dc.date.issued2013
dc.description.abstractEn la actualidad existe una tendencia por la construcción sustentable, también llamada construcción verde, la cual implica la utilización de materiales producidos con bajo consumo de energía. Es común el uso de materia prima proveniente de residuos o subproductos de fábricas industriales mediante la adición o la sustitución de componentes del concreto en diferentes proporciones. Este trabajo presenta las propiedades de un concreto fabricado con escoria de horno de cubilote (EHC) triturada. La arena se sustituyó por EHC en diferentes proporciones (0%, 10%, 15% y 20%). El residuo industrial se caracterizó físicamente respecto a su granulometría, densidad, absorción y humedad natural; con estos datos y los ensayos realizados al cemento, agua y los agregados pétreos seleccionados, se efectuó el diseño de la mezcla. Posteriormente se evaluó el comportamiento físico-mecánico del material compuesto, para una resistencia de diseño de 14 MPa. Se realizaron ensayos al concreto en estado fresco y en estado endurecido para determinar su resistencia a la compresión a diferentes edades para cada porcentaje de sustitución, el módulo de rotura, la velocidad inicial de absorción, la absorción, la carga de rotura, el módulo de elasticidad, la densidad del material endurecido y la masa unitaria. En cada prueba realizada en esta investigación, se tuvieron en cuenta las desviaciones estándar asociada a los resultados para la aceptación del ensayo. Se evidenció que el material compuesto presenta un comportamiento favorable en su resistencia a compresión al sustituir el 20% de arena por escoria. Se dedujo que a mayor porcentaje de sustitución de EHC menor es la resistencia a flexión. Los porcentajes de absorción del material compuesto resultaron mayores a los admisibles y respecto a la densidad, se concluyó que ésta guarda una relación proporcional con el porcentaje de sustitución.
dc.description.abstractenglishNowadays there is a sustentable construction trend also known as green construction, which involves the use of materials with low energy consumption. It's very common the use of materials which origin its from industrial plants using the addition or substitution of specific components in different proportions. The steel industry's debris its one of the best materials used as( value-added) and as cement material in the concrete. This study shows the concrete's properties with cupola furnace slag (EHC) crushed. The sand was replaced by EHC in different proportions (0%, 10%,15%, and 20%). The industrial residue was physically, characterized according with particle size, density and natural moisture absorption; using these data and the tests on cement, water and stone aggregates the mixture was design. Subsequently the physical-mechanical composite material's behavior for a design strength of 14 Mpa. Specific tests were made in the fresh and hard states to detemine its compressive strength at different times for each percentage of substitution, the rupture modulus, the initial rate of absorption, absorption, tensile strength, elasticity modulus, density of hardened material and unit weight. In each test made in this investigation always had present the standard deviations according with the acceptance for the test results. It showed that the composite has a favorable performance in compressive strength to replace 20% of slang sand. It appeared that a greater percentage of substitution of EHC lower flexural strength. The absortion percentages of the composite material were greater than those admisible for density and conclude that it stores proportional relation with substitution percentage.
dc.description.degreelevelMaestría
dc.description.degreenameMagíster en Ingeniería Civil
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/29661
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicomecánicas
dc.publisher.programMaestría en Ingeniería Civil
dc.publisher.schoolEscuela de Ingeniería Civil
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.subjectAgregado Fino
dc.subjectConcreto Modificado
dc.subjectEscoria
dc.subjectHorno De Cubilote
dc.subjectPropiedades Mecánicas.
dc.subject.keywordFine Aggregate
dc.subject.keywordModified Concrete
dc.subject.keywordSlag
dc.subject.keywordCupola Furnace
dc.subject.keywordMechanical Properties.
dc.titleUso de la escoria de procesos metalúrgicos como agregado del concreto para la fabricación de elementos de construcción no estructurales
dc.title.englishUsing process metallurgical slag as concrete added to manufacture nonstructural building elements
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_bdcc
dc.type.localTesis/Trabajo de grado - Monografía - Maestria
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
206.25 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
3.53 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
35.75 KB
Format:
Adobe Portable Document Format
Download
Collections
Maestría en Ingeniería Civil