Comportamiento del revestimiento de yeso modificado y su respuesta al proceso antioch

Simple item page
dc.contributor.advisorAlonso Baquero, Arnaldo
dc.contributor.authorSanabria González, Oscar Leonardo
dc.contributor.authorMartínez Banilla, Henry Jair
dc.date.accessioned2024-03-03T20:41:54Z
dc.date.available2014
dc.date.available2024-03-03T20:41:54Z
dc.date.created2014
dc.date.issued2014
dc.description.abstractEl yeso es un material cerámico abundante en la corteza terrestre, es empleado en diferentes industrias siendo la más destacada en joyería. La principal desventaja de los moldes de yeso para la elaboración de joyas es su baja permeabilidad, limitando el escape de los gases de la cavidad del molde durante la inyección del metal y su baja resistencia a altas temperaturas, además se debe someter a un tratamiento térmico a elevada temperatura (700 °C) para que se pueda completar la transformación del cuarzo y de la cristobalita, las cuales sufren fenómenos de expansión y contracción que afectan la estructura del molde causando fisuras. Estas limitantes pueden ser resueltas de varias formas, siendo la principal, usar composiciones especiales del molde y un tratamiento conocido como proceso Antioch. Una de la finalidad de este proceso es aumentar la permeabilidad de los moldes. De esta manera, se puede disminuir la temperatura de los moldes durante la colada (<370°C).Este proceso consiste en utilizar cerca de un 50% de arena refractaria mezclada con yeso y algunos aditivos para proporcionarle resistencia mecánica y estabilidad térmica a dicho revestimiento, calentar el molde en una autoclave (reactor que usa vapor sobrecalentado a presión), y después secar. Si los moldes sin secar son parcialmente deshidratados y luego dejados rehidratar sin interrumpir el proceso, los cristales recristalizan lentamente en forma de gránulos aproximadamente del tamaño de los granos de arena, y el molde adquiere una estructura porosa, de permeabilidad alta. El molde resultante tiene una permeabilidad considerable más grande, comparado con permeabilidades alrededor de 1 y 2 AFS obtenidas convencionalmente con moldes de yeso Este tipo de estudios tiene la finalidad de mejorar el pre-engaste en joyas, de esta manera se pretende aumentar el uso de esta técnica en la joyería local y un crecimiento de esta.
dc.description.abstractenglishGypsum is an abundant ceramic material in the earth's crust, is used in different industries being the most prominent in jewelry. The main disadvantage of plaster molds for making jewelry is its low permeability, limiting the escape of gases from the mold cavity during the injection of metal and low temperature resistance, must be subjected to further heat treatment at elevated temperature (700°C) so that it can complete the processing of quartz and cristobalite, which undergo expansion and contraction phenomena that affect the structure of the mold causing cracks. These limitations can be resolved in several ways, the main, use special mold compositions and treatment process known as Antioch. One purpose of this process is to increase the permeability of the molds. Thus, it may decrease the temperature of the mold during casting (< 370°C). This process is to use about 50% of refractory sand mixed with gypsum and some additives to provide mechanical strength and thermal stability to said coating, heating the mold in an autoclave ( reactor pressure using superheated steam), and then dried. If the molds are undried partially dehydrated and then rehydrated left without interrupting the crystals recrystallized slowly into pellets about the size of sand grains, and the mold takes a porous structure with high permeability. The resulting mold has a considerably larger permeability compared with permeabilities around 1 and 2 AFS conventionally obtained with plaster casts. This type of study is intended to improve the pre - crimping jewelry, so is to increase the use of this technique in the local jewelry and this growth.
dc.description.degreelevelPregrado
dc.description.degreenameIngeniero Metalúrgico
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/30478
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicoquímicas
dc.publisher.programIngeniería Metalúrgica
dc.publisher.schoolEscuela de Ingeniería Metalúrgica y Ciencia de Materiales
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.subjectPermeabilidad
dc.subjectResistencia A La Compresión En Seco
dc.subjectProceso Antioch
dc.subjectAutoclave.
dc.subject.keywordPermeability Fired Compressive Strength
dc.subject.keywordAntioch Process
dc.subject.keywordAutoclave.
dc.titleComportamiento del revestimiento de yeso modificado y su respuesta al proceso antioch
dc.title.englishBehavior of coating of modified plaster and its response to antioch process.
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_7a1f
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
310.04 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
2.9 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
565.13 KB
Format:
Adobe Portable Document Format
Download
Collections
Ingeniería Metalúrgica