Residuos generados por la autocombustión del carbón como materias primas en la preparación de materiales geopolimericos para promover el desarrollo de procesos industriales ambientalmente óptimos

Perea Contreras, Jairo Giovanni; Rincon Guarin, Hugo Andres

Publicación:
Residuos generados por la autocombustión del carbón como materias primas en la preparación de materiales geopolimericos para promover el desarrollo de procesos industriales ambientalmente óptimos

dc.contributor.advisor	Rios Reyes, Carlos Alberto
dc.contributor.advisor	Moreno Torres, Luis Eduardo
dc.contributor.author	Perea Contreras, Jairo Giovanni
dc.contributor.author	Rincon Guarin, Hugo Andres
dc.date.accessioned	2024-03-03T18:17:22Z
dc.date.available	2010
dc.date.available	2024-03-03T18:17:22Z
dc.date.created	2010
dc.date.issued	2010
dc.description.abstract	Se realizó una investigación con tipos de morteros siguiendo la norma Normas Técnicas Colombianas (Norma NTC 4630. 1999.) a). Se sustituyeron morteros al 5, 35, 70 y 95% con un material proveniente de la auto combustión del carbón (clinker) y b) morteros 100 % de cemento portland ordinario tipo I (CPO). Todos los sistemas se caracterizaron mecánicamente a 7, 14 y 28 días. En este trabajo se utilizó difracción de rayos X (DRX), Análisis granulométrico por tamizado, valor de azul de metileno en agregados finos, análisis de finura, se hallaron los pesos específicos, aparentes, nominal y absorción máxima que condicionan al material para un buen comportamiento en el desarrollo del geopolímero. Se genera una geopolimerización de materiales y la solución activante se preparo disolviendo hidróxido de sodio al 98% en pellets, la cual se mezcló con solución de silicato de sodio neutro 42 con relación molar SiO2:Na2O 3.0 (SiO2 = 28.74%, Na2O = 9.27%, y H2O = 61.99% en masa), Esta solución se preparo un día anterior al mezclado con el material de partida (clinker) y se fabricaron probetas de ensayo, las cuales fueron sometidas a pruebas tales como, resistencia a la compresión, ataque con acido sulfúrico (H2SO4), ataque con sulfato de magnesio (MgSO4) y sometidas a altas temperaturas (300ºC, 600ºC y 1000ºC), para evaluar y analizar su comportamiento, todas estas pruebas fueron tomadas de acuerdo a las normas ICONTEC e I.N.V.E
dc.description.abstractenglish	An investigation was conducted at rates following the standard mortar Colombian Technical Standards (Standard NTC 4630. 1999), a). Mortars were replaced at 5, 35, 70 and 95% with a self material from coal combustion (clinker) and b) mortars 100% of Type I ordinary portland cement (OPC). All systems were characterized mechanically to 7, 14 and 28 days. In this work we used X-ray diffraction (XRD), Particle size analysis by sieving, methylene blue value in fine aggregates, fine analysis, specific weights were found, apparently, nominal and maximum absorption material condition for good performance in Geopolymers development. Geopolimerización is generated material and activating solution was prepared by dissolving sodium hydroxide pellets 98%, which was mixed with sodium silicate solution 42 with neutral molar ratio SiO2: Na2O 3.0 (SiO2 = 28.74%, Na2O = 9.27% and 61.99% H2O = mass), This solution was prepared one day prior to mixing with the starting material (clinker) and test specimens were manufactured, which were subjected to tests such as compressive strength, attack with sulfuric acid (H2SO4), assault with magnesium sulphate (MgSO4) and subjected to high temperatures (300 °C, 600 °C and 1000 °C) to evaluate and analyze their behavior, All these tests were taken in agreement to the procedure ICONTEC and I.N.V.E
dc.description.degreelevel	Pregrado
dc.description.degreename	Geólogo
dc.format.mimetype	application/pdf
dc.identifier.instname	Universidad Industrial de Santander
dc.identifier.reponame	Universidad Industrial de Santander
dc.identifier.repourl	https://noesis.uis.edu.co
dc.identifier.uri	https://noesis.uis.edu.co/handle/20.500.14071/24540
dc.language.iso	spa
dc.publisher	Universidad Industrial de Santander
dc.publisher.faculty	Facultad de Ingenierías Fisicoquímicas
dc.publisher.program	Geología
dc.publisher.school	Escuela de Geología
dc.rights	http://creativecommons.org/licenses/by/4.0/
dc.rights.accessrights	info:eu-repo/semantics/openAccess
dc.rights.creativecommons	Atribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.license	Attribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.uri	http://creativecommons.org/licenses/by-nc/4.0
dc.subject	Geopolimerización
dc.subject	Geopolímero
dc.subject	Clinker natural
dc.subject	Cemento portland tipo I (CPO)
dc.subject	Curado
dc.subject	fraguado
dc.subject	morteros y probetas.
dc.subject.keyword	Geopolimerización
dc.subject.keyword	Geopolymers
dc.subject.keyword	Natural clinker
dc.subject.keyword	Portland cement type I (CPO)
dc.subject.keyword	Curing
dc.subject.keyword	mortars and cylinders.
dc.title	Residuos generados por la autocombustión del carbón como materias primas en la preparación de materiales geopolimericos para promover el desarrollo de procesos industriales ambientalmente óptimos
dc.title.english	Residuos generados por la autocombustion del carbon como materias primas en la preparacion de materiales geopolimericos para promover el desarrollo de procesos industriales ambientalmente optimos2
dc.type.coar	http://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversion	http://purl.org/coar/resource_type/c_7a1f
dc.type.local	Tesis/Trabajo de grado - Monografía - Pregrado
dspace.entity.type	Publication