Síntesis y caracterización de las propiedades fisicomecanicas de geopolimeros a partir de puzolana para su aplicación en la industria

Simple item page
dc.contributor.advisorRios Reyes, Carlos
dc.contributor.advisorMoreno Torres, Luis Eduardo
dc.contributor.authorÁlvarez Mantilla, Hernando
dc.date.accessioned2024-03-03T18:17:22Z
dc.date.available2010
dc.date.available2024-03-03T18:17:22Z
dc.date.created2010
dc.date.issued2010
dc.description.abstractLas tendencias mundiales en la industria de la construcción y grupos de investigación se encaminan hacia el uso de materiales alternativos que favorezcan el desarrollo sostenible con una baja emisión de CO2 y correcto aprovechamiento de los recursos naturales, acompañado de ventajas técnicas para su versatilidad en diferentes campos de aplicación El presente trabajo consiste en la evaluación del desempeño de morteros geopoliméricos obtenidos a partir de la activación alcalina de una puzolana natural. Como activador alcalino para la producción de los morteros geopoliméricos se empleó hidróxido de sodio (NaOH) con una concentración 8M y silicato de sodio semineutro 42 (Na2SiO3) con una relación molar de SiO2: NaO = 3.0. Los materiales cementantes fueron sometidos a pruebas de resistencia mecánica y de durabilidad, esta última con relación a su resistencia al ataque con acido sulfúrico (H2SO4) y sulfato de magnesio (MgSO4), así como a altas temperaturas; la prueba de resistencia a la compresión se realizó hasta 80 días de curado y la de durabilidad hasta 9 semanas de estar inmersas en dichas soluciones. Para todas estas pruebas se determinó la pérdida de peso y de resistencia a la compresión expresadas en porcentajes; finalmente se hace una comparación del desempeño de los morteros geopoliméricos a base de puzolana natural con respecto al desempeño de morteros preparados con cemento portland ordinario expuestos a las mismas condiciones. Las pruebas realizadas a las probetas se llevaron a cabo siguiendo los procedimientos especificados en la Norma Técnica Colombiana ICONTEC NTC 220 fiDeterminación de la resistencia de morteros de cemento hidráulico usando cubos de mortero de 50 mm de ladofl
dc.description.abstractenglishGlobal trends in the construction industry and research groups are moving towards the use of alternative materials which promote sustainable development with low CO2 emissions and proper use of natural resources, along with technical advantages in order to expand to different fields of application. This work concerns the performance assessment of the geopolymeric mortars obtained from the alkaline activation of natural pozzolan. Sodium hydroxide (NaOH) at an 8M concentration and sodium silicate (Na2SiO3) grade 42, with a molar ratio of SiO2 to NaO equal to 3.0, were used as an alkaline activator for the production of geoplymeric mortars. The cementitious materials were tested for mechanical strength and durability, the latter in relation to its resistance to attack by sulfuric acid (H2SO4) and magnesium sulfate (MgSO4), as well as high temperatures. The test for compressive strength was conducted up to 80 days of curing, and the durability test took up to 9 weeks of immersion in such solutions. The weight loss and the compressive strength were calculated for all the tests and the information was expressed as several percentages. Finally, the performance of the geopolymeric mortars from natural pozzolan was compared to the performance of ordinary Portland cement mortars subjected to the same conditions. All tests were carried out according to the procedures specified in ICONTEC Colombian Technical Standard NTC 220 "Determination of the resistance for hydraulic cement mortars using 50 mm sideway mortar cubes
dc.description.degreelevelPregrado
dc.description.degreenameGeólogo
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/24542
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicoquímicas
dc.publisher.programGeología
dc.publisher.schoolEscuela de Geología
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.subjectGeopolímeros
dc.subjectPuzolana
dc.subjectActivación alcalina.
dc.subject.keywordGeopolymer
dc.subject.keywordPozzolan
dc.subject.keywordAlkali
dc.titleSíntesis y caracterización de las propiedades fisicomecanicas de geopolimeros a partir de puzolana para su aplicación en la industria
dc.title.englishSynthesis and characterization of the physical and mechanical geopolymeric properties from pozzolan for industrial applications
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_7a1f
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
283.72 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
2.87 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
266.62 KB
Format:
Adobe Portable Document Format
Download
Collections
Geología