Evaluación del comportamiento a la corrosión de una varilla de acero galvanizado en concreto reforzado con diferentes concentraciones de cloruros y carbonatos

Simple item page
dc.contributor.advisorCruz Hernández, Ricardo Alfredo
dc.contributor.advisorPeña Ballesteros, Darío Yesid
dc.contributor.authorBarrabagan Cárdenas, Ana Yibe
dc.contributor.authorArciniegas Estepa, Jully Andrea
dc.date.accessioned2024-03-03T19:32:46Z
dc.date.available2012
dc.date.available2024-03-03T19:32:46Z
dc.date.created2012
dc.date.issued2012
dc.description.abstractLa corrosión del refuerzo en el concreto conduce a la formación de grietas y reduce la vida útil de la estructura. La carbonatación después del ataque por cloruros es la segunda causa de corrosión del refuerzo en estructuras civiles. El objetivo de esta investigación fue evaluar el efecto de la carbonatación y el ion cloruro en probetas con acero reforzado, galvanizadas y sin galvanizar para el respectivo análisis, a diferentes concentraciones de cloruros y carbonatos mediante técnicas electroquímicas tales como: LPR, EIS, Pulso Galvanostático, OCP. Con una relación agua/cemento de 0.5, probetas con 28 días de curado en agua sal a una concentración de 3.5% y 4.5% de NaCl, y con un proceso de humectación y secado cada 24 horas, fueron sometidas a un proceso de carbonatación acelerada, esta prueba se llevó a cabo en un ambiente del 70 % de CO2 y una Humedad Relativa entre 50 y 65 % a una temperatura de 25°C. Se evaluaron los cambios en el concreto reforzado debidos a la reacción de carbonatación y la penetración del ion cloruro, además de las técnicas electroquímicas mencionadas anteriormente, con el fin de obtener mayores resultados se realizaron pruebas de inspección visual, resistencia a la compresión, y ataque químico con fenolftaleína. De acuerdo con los ensayos realizados se observa la influencia de la carbonatación, en la capacidad de penetración del ion cloruro a través de la matriz cementicia. Mediante el análisis de resultados electroquímicos, se observó la influencia directa de la concentración de cloruros y la concentración de carbonatos en las velocidades de corrosión, las cuales fueron controladas en el tiempo a través de mediciones de resistencia a la polarización mostrando una clara diferencia en el comportamiento de corrosión con refuerzo galvanizado y sin galvanizar.
dc.description.abstractenglishReinforcement corrosion in concrete, leads to the formation of cracks and reduces the useful life of the structure. After carbonation, chloride attack is the second cause of corrosion of reinforcement in civil structures. The objective of this research was to evaluate the effect of carbonation and chloride ion in test tubes with reinforced steel, galvanized and not galvanized for the respective analysis to different concentrations of chlorides and carbonates using electrochemical techniques such as LPR, EIS, Galvanostatic Pulse, and OCP. With a water / cement ratio of 0.5, test tubes that had spent 28 days of curing in salt water at a concentration of 3.5% and 4.5% NaCl, and a process of humidification and drying each 24 hours, respectively, were subjected to a process of accelerated carbonation, this test was taken in an atmosphere of 70% CO 2 and a relative humidity between 50 and 65% at a temperature of 25 ° C. Changes in reinforced concrete were assessed due to carbonation reaction and chloride ion penetration. In addition to the electrochemical techniques mentioned before, in order to obtain better results, visual inspection, compressive strength, and attack with chemical phenolphthalein tests were taken. According to the tests performed, it is appreciated the influence of carbonation in the chloride ion penetration ability through the cement matrix. By analysis of the electrochemical results, it was observed the direct influence of the chloride concentration and the concentration of carbonate in the corrosion rates, which were controlled in time through measurements of polarization resistance, showing a clear difference in the corrosion behavior between galvanized reinforcement and
dc.description.degreelevelPregrado
dc.description.degreenameIngeniero Civil
dc.format.mimetypeapplication/pdf
dc.identifier.instnameUniversidad Industrial de Santander
dc.identifier.reponameUniversidad Industrial de Santander
dc.identifier.repourlhttps://noesis.uis.edu.co
dc.identifier.urihttps://noesis.uis.edu.co/handle/20.500.14071/27135
dc.language.isospa
dc.publisherUniversidad Industrial de Santander
dc.publisher.facultyFacultad de Ingenierías Fisicomecánicas
dc.publisher.programIngeniería Civil
dc.publisher.schoolEscuela de Ingeniería Civil
dc.rightshttp://creativecommons.org/licenses/by/4.0/
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)
dc.rights.licenseAttribution-NonCommercial 4.0 International (CC BY-NC 4.0)
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0
dc.subjectConcreto reforzado
dc.subjectAcero galvanizado
dc.subjectCorrosión
dc.subjectCarbonatación
dc.subjectCloruros
dc.subjecttécnicas
dc.subject.keywordReinforced concrete
dc.subject.keywordGalvanized steel
dc.subject.keywordCorrosion
dc.subject.keywordCarbonation
dc.subject.keywordChloride
dc.subject.keywordelectrochemical
dc.titleEvaluación del comportamiento a la corrosión de una varilla de acero galvanizado en concreto reforzado con diferentes concentraciones de cloruros y carbonatos
dc.title.englishEvaluation about the corrosion behaviour of a galvanized steel rod in reinforced concrete with different concentrations of chloride and
dc.type.coarhttp://purl.org/coar/version/c_b1a7d7d4d402bcce
dc.type.hasversionhttp://purl.org/coar/resource_type/c_7a1f
dc.type.localTesis/Trabajo de grado - Monografía - Pregrado
Files
Original bundle
Now showing 1 - 3 of 3
No Thumbnail Available
Name:
Carta de autorización.pdf
Size:
624.53 KB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Documento.pdf
Size:
4.99 MB
Format:
Adobe Portable Document Format
Download
No Thumbnail Available
Name:
Nota de proyecto.pdf
Size:
517.58 KB
Format:
Adobe Portable Document Format
Download
Collections
Ingeniería Civil