Corrosion a alta temperatura de un acero 2.25cr-1mo en contacto con una mezcla de k2so4-nacl
| dc.contributor.advisor | Peña Ballesteros, Darío Yesid | |
| dc.contributor.author | Cáceres Jiménez, Andrea | |
| dc.contributor.author | Camargo Hernández, Nelson Adolfo | |
| dc.date.accessioned | 2024-03-03T04:39:39Z | |
| dc.date.available | 2004 | |
| dc.date.available | 2024-03-03T04:39:39Z | |
| dc.date.created | 2004 | |
| dc.date.issued | 2004 | |
| dc.description.abstract | El acero ferritico 2.25Cr-1Mo es comunmente utilizado para la fabricación de tubos de supercalentadores para calderas industriales debido a las buenas propiedades mecánicas a alta temperatura. Sin embargo, las cenizas producidas por el combustible quemado se depositan sobre la superficie de estos componentes provocando corrosión en caliente debido al contenido de cloruros y sulfatos presentes. La oxidación es otro fenómeno que puede perjudicar la vida útil de estos componentes, cuando ésta es combinada con la corrosión en caliente aparecen fenómenos de corrosión aclerada. En esta investigación se evaluó la oxidación sobre el acero 2.25Cr-1Mo y el efecto de la mezcla de sales 40%K2SO4-60%NaCl a temperaturas de exposición entre 550ºC y 650ºC, utilizando la norma estandarizada por la Federación Europea de Corrosión. Ganancia de peso Vs tiempo a diferentes temperaturas fueron registrados para evaluar el efecto corrosivo de la mezcla de sales. Análisis de DRX, análisis de metalografía y ensayos de dureza fueron realizados para identificar los productos de corrosión y el posible cambio microestructural. Además, fue evaluada la constante de velocidad de corrosión determinando así la energía de activación del proceso y por lo tanto, el posible mecanismo de corrosión. Se observó que la velocidad de corrosión aumentó con el incremento del tiempo y la temperatura de exposición, mostrando un comportamiento parabólico, lo que indica un proceso corrosivo por difusión, con una energía de activación de 15,47Kcal. | |
| dc.description.abstractenglish | 2.25Cr-1Mo ferritic steel is commonly used for the production of superheathers tubes for industrial boilers due to the good mechanical properties at high temperature. However, the ashes burnt by fuel can be deposited on the surface of these components causing hot corrosion due to their contains of chlorides and sulfates. The oxidation is another phenomenon that can harm the useful life of these components, when it is combined by hot corrosion, can appear corrosion accelerate. In this research the oxidation and the effect of the mixture of salts 40%K2SO4-60%NaCl on the 2,25Cr-1Mo steel were evaluated to temperatures between 550ºC and 650ºC, by using the technical standars by the European Federation of Corrosion. Mass gain Vs time at different temperatures was registered to evaluate the corrosive effect of the mixture of salts. Analysis of DRX, metalographic analysis and test hardness were carried out to identify the products of corrosion and the possible microestructural changes. Also, the corrosion constant kp was evaluated by determining the activation energy of the process and therefore, the possible mechanism of corrosion. It was observed that the corrosion rate increased with the increment of the time exposure and temperature, showing a parabolic behavior, the corrosion mechanism was controlled by a diffusion process, with an activation global energy of 15,47Kcal. | |
| dc.description.degreelevel | Pregrado | |
| dc.description.degreename | Ingeniero Metalúrgico | |
| dc.format.mimetype | application/pdf | |
| dc.identifier.instname | Universidad Industrial de Santander | |
| dc.identifier.reponame | Universidad Industrial de Santander | |
| dc.identifier.repourl | https://noesis.uis.edu.co | |
| dc.identifier.uri | https://noesis.uis.edu.co/handle/20.500.14071/16520 | |
| dc.language.iso | spa | |
| dc.publisher | Universidad Industrial de Santander | |
| dc.publisher.faculty | Facultad de Ingenierías Fisicoquímicas | |
| dc.publisher.program | Ingeniería Metalúrgica | |
| dc.publisher.school | Escuela de Ingeniería Metalúrgica y Ciencia de Materiales | |
| dc.rights | http://creativecommons.org/licenses/by/4.0/ | |
| dc.rights.accessrights | info:eu-repo/semantics/openAccess | |
| dc.rights.creativecommons | Atribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0) | |
| dc.rights.license | Attribution-NonCommercial 4.0 International (CC BY-NC 4.0) | |
| dc.rights.uri | http://creativecommons.org/licenses/by-nc/4.0 | |
| dc.subject | Corrosión por sales fundidas | |
| dc.subject | Acero 2.25Cr-1Mo | |
| dc.subject | Energía de activación | |
| dc.subject | Pérdida de peso. | |
| dc.subject.keyword | Corrosion for fused salts | |
| dc.subject.keyword | 2.25Cr-1Mo ferritic steel | |
| dc.subject.keyword | Activation energy | |
| dc.subject.keyword | Loss of weight. | |
| dc.title | Corrosion a alta temperatura de un acero 2.25cr-1mo en contacto con una mezcla de k2so4-nacl | |
| dc.title.english | High temperature corrosion of 2.25cr-1mo steel in contact with a mixture of k2so4-nacl | |